C47940 Brass vs. Z20301 Zinc
C47940 brass belongs to the copper alloys classification, while Z20301 zinc belongs to the zinc alloys. They have a modest 31% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C47940 brass and the bottom bar is Z20301 zinc.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 87 |
| Elongation at Break, % | 14 to 34 | |
| 53 |
| Poisson's Ratio | 0.31 | |
| 0.25 |
| Shear Modulus, GPa | 40 | |
| 35 |
| Tensile Strength: Ultimate (UTS), MPa | 380 to 520 | |
| 160 |
| Tensile Strength: Yield (Proof), MPa | 160 to 390 | |
| 130 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 110 |
| Maximum Temperature: Mechanical, °C | 130 | |
| 90 |
| Melting Completion (Liquidus), °C | 850 | |
| 410 |
| Melting Onset (Solidus), °C | 800 | |
| 400 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 390 |
| Thermal Conductivity, W/m-K | 110 | |
| 110 |
| Thermal Expansion, µm/m-K | 20 | |
| 26 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 25 | |
| 11 |
| Density, g/cm3 | 8.2 | |
| 6.6 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 2.8 |
| Embodied Energy, MJ/kg | 47 | |
| 53 |
| Embodied Water, L/kg | 330 | |
| 340 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 68 to 100 | |
| 78 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 to 740 | |
| 96 |
| Stiffness to Weight: Axial, points | 7.1 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 19 | |
| 23 |
| Strength to Weight: Axial, points | 13 to 17 | |
| 6.7 |
| Strength to Weight: Bending, points | 14 to 17 | |
| 9.9 |
| Thermal Diffusivity, mm2/s | 36 | |
| 44 |
| Thermal Shock Resistance, points | 13 to 17 | |
| 5.0 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 0.0020 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.010 |
| Copper (Cu), % | 63 to 66 | |
| 0 to 0.0050 |
| Iron (Fe), % | 0.1 to 1.0 | |
| 0 to 0.010 |
| Lead (Pb), % | 1.0 to 2.0 | |
| 0 to 0.1 |
| Nickel (Ni), % | 0.1 to 0.5 | |
| 0 |
| Tin (Sn), % | 1.2 to 2.0 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.020 |
| Zinc (Zn), % | 28.1 to 34.6 | |
| 99.853 to 100 |
| Residuals, % | 0 to 0.4 | |
| 0 |