C48200 Brass vs. Solder Alloy 301
C48200 brass belongs to the copper alloys classification, while solder alloy 301 belongs to the otherwise unclassified metals. There are 25 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C48200 brass and the bottom bar is solder alloy 301.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 40 |
| Elongation at Break, % | 15 to 40 | |
| 51 |
| Poisson's Ratio | 0.31 | |
| 0.34 |
| Shear Modulus, GPa | 40 | |
| 15 |
| Tensile Strength: Ultimate (UTS), MPa | 400 to 500 | |
| 55 |
| Tensile Strength: Yield (Proof), MPa | 160 to 320 | |
| 49 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 55 |
| Melting Completion (Liquidus), °C | 900 | |
| 140 |
| Melting Onset (Solidus), °C | 890 | |
| 140 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 160 |
| Thermal Conductivity, W/m-K | 120 | |
| 19 |
| Thermal Expansion, µm/m-K | 21 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 26 | |
| 4.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 29 | |
| 4.9 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.0 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 13 |
| Embodied Energy, MJ/kg | 47 | |
| 210 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 61 to 140 | |
| 27 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 to 500 | |
| 30 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 2.5 |
| Stiffness to Weight: Bending, points | 19 | |
| 13 |
| Strength to Weight: Axial, points | 14 to 17 | |
| 1.8 |
| Strength to Weight: Bending, points | 15 to 17 | |
| 3.7 |
| Thermal Diffusivity, mm2/s | 38 | |
| 13 |
| Thermal Shock Resistance, points | 13 to 16 | |
| 7.2 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 0.0010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.1 |
| Arsenic (As), % | 0 | |
| 0 to 0.030 |
| Bismuth (Bi), % | 0 | |
| 56.5 to 59 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0020 |
| Copper (Cu), % | 59 to 62 | |
| 0 to 0.050 |
| Gold (Au), % | 0 | |
| 0 to 0.050 |
| Indium (In), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.020 |
| Lead (Pb), % | 0.4 to 1.0 | |
| 0 to 0.070 |
| Nickel (Ni), % | 0 | |
| 0 to 0.010 |
| Silver (Ag), % | 0 | |
| 0 to 0.1 |
| Tin (Sn), % | 0.5 to 1.0 | |
| 41 to 43 |
| Zinc (Zn), % | 35.5 to 40.1 | |
| 0 to 0.0010 |
| Residuals, % | 0 to 0.4 | |
| 0 |