C48500 Brass vs. EN 1.4542 Stainless Steel
C48500 brass belongs to the copper alloys classification, while EN 1.4542 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C48500 brass and the bottom bar is EN 1.4542 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 190 |
| Elongation at Break, % | 13 to 40 | |
| 5.7 to 20 |
| Poisson's Ratio | 0.31 | |
| 0.28 |
| Shear Modulus, GPa | 39 | |
| 76 |
| Shear Strength, MPa | 250 to 300 | |
| 550 to 860 |
| Tensile Strength: Ultimate (UTS), MPa | 400 to 500 | |
| 880 to 1470 |
| Tensile Strength: Yield (Proof), MPa | 160 to 320 | |
| 580 to 1300 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 860 |
| Melting Completion (Liquidus), °C | 900 | |
| 1430 |
| Melting Onset (Solidus), °C | 890 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 470 |
| Thermal Conductivity, W/m-K | 120 | |
| 16 |
| Thermal Expansion, µm/m-K | 21 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 26 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 29 | |
| 2.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 13 |
| Density, g/cm3 | 8.1 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.7 |
| Embodied Energy, MJ/kg | 46 | |
| 39 |
| Embodied Water, L/kg | 330 | |
| 130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 56 to 140 | |
| 62 to 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 to 500 | |
| 880 to 4360 |
| Stiffness to Weight: Axial, points | 7.1 | |
| 14 |
| Stiffness to Weight: Bending, points | 19 | |
| 25 |
| Strength to Weight: Axial, points | 14 to 17 | |
| 31 to 52 |
| Strength to Weight: Bending, points | 15 to 17 | |
| 26 to 37 |
| Thermal Diffusivity, mm2/s | 38 | |
| 4.3 |
| Thermal Shock Resistance, points | 13 to 17 | |
| 29 to 49 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 | |
| 0 to 0.070 |
| Chromium (Cr), % | 0 | |
| 15 to 17 |
| Copper (Cu), % | 59 to 62 | |
| 3.0 to 5.0 |
| Iron (Fe), % | 0 to 0.1 | |
| 69.6 to 79 |
| Lead (Pb), % | 1.3 to 2.2 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.6 |
| Nickel (Ni), % | 0 | |
| 3.0 to 5.0 |
| Niobium (Nb), % | 0 | |
| 0 to 0.45 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 0 to 0.7 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Tin (Sn), % | 0.5 to 1.0 | |
| 0 |
| Zinc (Zn), % | 34.3 to 39.2 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 |