C48500 Brass vs. C67500 Bronze
Both C48500 brass and C67500 bronze are copper alloys. They have a very high 96% of their average alloy composition in common.
For each property being compared, the top bar is C48500 brass and the bottom bar is C67500 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 100 |
| Elongation at Break, % | 13 to 40 | |
| 14 to 33 |
| Poisson's Ratio | 0.31 | |
| 0.3 |
| Shear Modulus, GPa | 39 | |
| 40 |
| Shear Strength, MPa | 250 to 300 | |
| 270 to 350 |
| Tensile Strength: Ultimate (UTS), MPa | 400 to 500 | |
| 430 to 580 |
| Tensile Strength: Yield (Proof), MPa | 160 to 320 | |
| 170 to 370 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 120 |
| Melting Completion (Liquidus), °C | 900 | |
| 890 |
| Melting Onset (Solidus), °C | 890 | |
| 870 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 390 |
| Thermal Conductivity, W/m-K | 120 | |
| 110 |
| Thermal Expansion, µm/m-K | 21 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 26 | |
| 24 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 29 | |
| 27 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 23 |
| Density, g/cm3 | 8.1 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.8 |
| Embodied Energy, MJ/kg | 46 | |
| 47 |
| Embodied Water, L/kg | 330 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 56 to 140 | |
| 61 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 to 500 | |
| 130 to 650 |
| Stiffness to Weight: Axial, points | 7.1 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 19 | |
| 20 |
| Strength to Weight: Axial, points | 14 to 17 | |
| 15 to 20 |
| Strength to Weight: Bending, points | 15 to 17 | |
| 16 to 19 |
| Thermal Diffusivity, mm2/s | 38 | |
| 34 |
| Thermal Shock Resistance, points | 13 to 17 | |
| 14 to 19 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 0.25 |
| Copper (Cu), % | 59 to 62 | |
| 57 to 60 |
| Iron (Fe), % | 0 to 0.1 | |
| 0.8 to 2.0 |
| Lead (Pb), % | 1.3 to 2.2 | |
| 0 to 0.2 |
| Manganese (Mn), % | 0 | |
| 0.050 to 0.5 |
| Tin (Sn), % | 0.5 to 1.0 | |
| 0.5 to 1.5 |
| Zinc (Zn), % | 34.3 to 39.2 | |
| 35.1 to 41.7 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.5 |