C50100 Bronze vs. A360.0 Aluminum

C50100 bronze belongs to the copper alloys classification, while A360.0 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is C50100 bronze and the bottom bar is A360.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
72
Elongation at Break, % 40
1.6 to 5.0
Poisson's Ratio 0.34
0.33
Shear Modulus, GPa 43
27
Shear Strength, MPa 180
180
Tensile Strength: Ultimate (UTS), MPa 270
180 to 320
Tensile Strength: Yield (Proof), MPa 82
170 to 260

Thermal Properties

Latent Heat of Fusion, J/g 210
530
Maximum Temperature: Mechanical, °C 200
170
Melting Completion (Liquidus), °C 1080
680
Melting Onset (Solidus), °C 1070
590
Specific Heat Capacity, J/kg-K 380
900
Thermal Conductivity, W/m-K 230
110
Thermal Expansion, µm/m-K 17
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 55
30
Electrical Conductivity: Equal Weight (Specific), % IACS 55
100

Otherwise Unclassified Properties

Base Metal Price, % relative 31
9.5
Density, g/cm3 8.9
2.6
Embodied Carbon, kg CO2/kg material 2.6
7.8
Embodied Energy, MJ/kg 42
150
Embodied Water, L/kg 310
1070

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 82
4.6 to 13
Resilience: Unit (Modulus of Resilience), kJ/m3 29
190 to 470
Stiffness to Weight: Axial, points 7.2
15
Stiffness to Weight: Bending, points 18
53
Strength to Weight: Axial, points 8.3
19 to 34
Strength to Weight: Bending, points 10
27 to 39
Thermal Diffusivity, mm2/s 66
48
Thermal Shock Resistance, points 9.5
8.5 to 15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
85.8 to 90.6
Copper (Cu), % 98.6 to 99.49
0 to 0.6
Iron (Fe), % 0 to 0.050
0 to 1.3
Lead (Pb), % 0 to 0.050
0
Magnesium (Mg), % 0
0.4 to 0.6
Manganese (Mn), % 0
0 to 0.35
Nickel (Ni), % 0
0 to 0.5
Phosphorus (P), % 0.010 to 0.050
0
Silicon (Si), % 0
9.0 to 10
Tin (Sn), % 0.5 to 0.8
0 to 0.15
Zinc (Zn), % 0
0 to 0.5
Residuals, % 0 to 0.5
0 to 0.25