C50100 Bronze vs. ASTM B631 Class C

C50100 bronze belongs to the copper alloys classification, while ASTM B631 class C belongs to the otherwise unclassified metals. There are 16 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is C50100 bronze and the bottom bar is ASTM B631 class C.

UNS C50100 Phosphor Bronze ASTM B631 Class C Silver-Tungsten Electrical Contact Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		120
Elastic (Young's, Tensile) Modulus, GPa		180 to 190

Poisson's Ratio		0.34
Poisson's Ratio		0.32

Shear Modulus, GPa		43
Shear Modulus, GPa		66 to 71

Thermal Properties

Latent Heat of Fusion, J/g		210
Latent Heat of Fusion, J/g		140 to 150

Melting Completion (Liquidus), °C		1080
Melting Completion (Liquidus), °C		2090 to 2230

Specific Heat Capacity, J/kg-K		380
Specific Heat Capacity, J/kg-K		180

Thermal Conductivity, W/m-K		230
Thermal Conductivity, W/m-K		450 to 490

Thermal Expansion, µm/m-K		17
Thermal Expansion, µm/m-K		14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS		55
Electrical Conductivity: Equal Volume, % IACS		55 to 63

Electrical Conductivity: Equal Weight (Specific), % IACS		55
Electrical Conductivity: Equal Weight (Specific), % IACS		36 to 43

Otherwise Unclassified Properties

Density, g/cm³		8.9
Density, g/cm³		13 to 14

Embodied Carbon, kg CO₂/kg material		2.6
Embodied Carbon, kg CO₂/kg material		55 to 59

Embodied Energy, MJ/kg		42
Embodied Energy, MJ/kg		860 to 920

Common Calculations

Stiffness to Weight: Axial, points		7.2
Stiffness to Weight: Axial, points		7.4 to 7.6

Stiffness to Weight: Bending, points		18
Stiffness to Weight: Bending, points		14

Thermal Diffusivity, mm²/s		66
Thermal Diffusivity, mm²/s		180 to 200