C50100 Bronze vs. AWS E309LMo

C50100 bronze belongs to the copper alloys classification, while AWS E309LMo belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is C50100 bronze and the bottom bar is AWS E309LMo.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
200
Elongation at Break, % 40
34
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 43
79
Tensile Strength: Ultimate (UTS), MPa 270
580

Thermal Properties

Latent Heat of Fusion, J/g 210
300
Melting Completion (Liquidus), °C 1080
1430
Melting Onset (Solidus), °C 1070
1390
Specific Heat Capacity, J/kg-K 380
480
Thermal Conductivity, W/m-K 230
15
Thermal Expansion, µm/m-K 17
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 55
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 55
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 31
22
Density, g/cm3 8.9
7.9
Embodied Carbon, kg CO2/kg material 2.6
4.2
Embodied Energy, MJ/kg 42
59
Embodied Water, L/kg 310
180

Common Calculations

Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 18
25
Strength to Weight: Axial, points 8.3
21
Strength to Weight: Bending, points 10
20
Thermal Diffusivity, mm2/s 66
3.9
Thermal Shock Resistance, points 9.5
15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.040
Chromium (Cr), % 0
22 to 25
Copper (Cu), % 98.6 to 99.49
0 to 0.75
Iron (Fe), % 0 to 0.050
53.6 to 63.5
Lead (Pb), % 0 to 0.050
0
Manganese (Mn), % 0
0.5 to 2.5
Molybdenum (Mo), % 0
2.0 to 3.0
Nickel (Ni), % 0
12 to 14
Phosphorus (P), % 0.010 to 0.050
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 0.5 to 0.8
0
Residuals, % 0 to 0.5
0