C50100 Bronze vs. EN 1.4948 Stainless Steel

C50100 bronze belongs to the copper alloys classification, while EN 1.4948 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is C50100 bronze and the bottom bar is EN 1.4948 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
200
Elongation at Break, % 40
48
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 43
77
Shear Strength, MPa 180
430
Tensile Strength: Ultimate (UTS), MPa 270
610
Tensile Strength: Yield (Proof), MPa 82
210

Thermal Properties

Latent Heat of Fusion, J/g 210
290
Maximum Temperature: Mechanical, °C 200
930
Melting Completion (Liquidus), °C 1080
1430
Melting Onset (Solidus), °C 1070
1380
Specific Heat Capacity, J/kg-K 380
480
Thermal Conductivity, W/m-K 230
17
Thermal Expansion, µm/m-K 17
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 55
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 55
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 31
15
Density, g/cm3 8.9
7.8
Embodied Carbon, kg CO2/kg material 2.6
3.0
Embodied Energy, MJ/kg 42
43
Embodied Water, L/kg 310
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 82
230
Resilience: Unit (Modulus of Resilience), kJ/m3 29
110
Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 18
25
Strength to Weight: Axial, points 8.3
22
Strength to Weight: Bending, points 10
21
Thermal Diffusivity, mm2/s 66
4.5
Thermal Shock Resistance, points 9.5
14

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.040 to 0.080
Chromium (Cr), % 0
17 to 19
Copper (Cu), % 98.6 to 99.49
0
Iron (Fe), % 0 to 0.050
66.8 to 75
Lead (Pb), % 0 to 0.050
0
Manganese (Mn), % 0
0 to 2.0
Nickel (Ni), % 0
8.0 to 11
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0.010 to 0.050
0 to 0.035
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.015
Tin (Sn), % 0.5 to 0.8
0
Residuals, % 0 to 0.5
0