C50100 bronze belongs to the copper alloys classification, while EN 1.5026 steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is C50100 bronze and the bottom bar is EN 1.5026 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
190
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 43
72
Tensile Strength: Ultimate (UTS), MPa 270
660 to 1980

Thermal Properties

Latent Heat of Fusion, J/g 210
280
Maximum Temperature: Mechanical, °C 200
400
Melting Completion (Liquidus), °C 1080
1440
Melting Onset (Solidus), °C 1070
1390
Specific Heat Capacity, J/kg-K 380
480
Thermal Conductivity, W/m-K 230
47
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 55
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 55
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 31
1.9
Density, g/cm3 8.9
7.7
Embodied Carbon, kg CO2/kg material 2.6
1.5
Embodied Energy, MJ/kg 42
19
Embodied Water, L/kg 310
46

Common Calculations

Stiffness to Weight: Axial, points 7.2
13
Stiffness to Weight: Bending, points 18
25
Strength to Weight: Axial, points 8.3
24 to 71
Strength to Weight: Bending, points 10
22 to 45
Thermal Diffusivity, mm2/s 66
13
Thermal Shock Resistance, points 9.5
20 to 60

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.52 to 0.6
Copper (Cu), % 98.6 to 99.49
0
Iron (Fe), % 0 to 0.050
96.5 to 97.3
Lead (Pb), % 0 to 0.050
0
Manganese (Mn), % 0
0.6 to 0.9
Phosphorus (P), % 0.010 to 0.050
0 to 0.025
Silicon (Si), % 0
1.6 to 2.0
Sulfur (S), % 0
0 to 0.025
Tin (Sn), % 0.5 to 0.8
0
Residuals, % 0 to 0.5
0