C50100 Bronze vs. EN 1.7710 Steel

C50100 bronze belongs to the copper alloys classification, while EN 1.7710 steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is C50100 bronze and the bottom bar is EN 1.7710 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
190
Elongation at Break, % 40
6.8 to 11
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 43
73
Tensile Strength: Ultimate (UTS), MPa 270
930 to 1070
Tensile Strength: Yield (Proof), MPa 82
800 to 1060

Thermal Properties

Latent Heat of Fusion, J/g 210
260
Maximum Temperature: Mechanical, °C 200
440
Melting Completion (Liquidus), °C 1080
1470
Melting Onset (Solidus), °C 1070
1430
Specific Heat Capacity, J/kg-K 380
470
Thermal Conductivity, W/m-K 230
41
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 55
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 55
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 31
3.5
Density, g/cm3 8.9
7.8
Embodied Carbon, kg CO2/kg material 2.6
2.2
Embodied Energy, MJ/kg 42
30
Embodied Water, L/kg 310
57

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 82
73 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 29
1680 to 2970
Stiffness to Weight: Axial, points 7.2
13
Stiffness to Weight: Bending, points 18
24
Strength to Weight: Axial, points 8.3
33 to 38
Strength to Weight: Bending, points 10
27 to 30
Thermal Diffusivity, mm2/s 66
11
Thermal Shock Resistance, points 9.5
27 to 31

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.12 to 0.18
Chromium (Cr), % 0
1.3 to 1.8
Copper (Cu), % 98.6 to 99.49
0
Iron (Fe), % 0 to 0.050
95.1 to 97
Lead (Pb), % 0 to 0.050
0
Manganese (Mn), % 0
0.6 to 1.0
Molybdenum (Mo), % 0
0.8 to 1.0
Phosphorus (P), % 0.010 to 0.050
0 to 0.025
Silicon (Si), % 0
0 to 0.6
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 0.5 to 0.8
0
Vanadium (V), % 0
0.15 to 0.25
Residuals, % 0 to 0.5
0