C50100 Bronze vs. EN AC-45400 Aluminum

C50100 bronze belongs to the copper alloys classification, while EN AC-45400 aluminum belongs to the aluminum alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is C50100 bronze and the bottom bar is EN AC-45400 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
72
Elongation at Break, % 40
6.7
Poisson's Ratio 0.34
0.33
Shear Modulus, GPa 43
27
Tensile Strength: Ultimate (UTS), MPa 270
260
Tensile Strength: Yield (Proof), MPa 82
130

Thermal Properties

Latent Heat of Fusion, J/g 210
470
Maximum Temperature: Mechanical, °C 200
170
Melting Completion (Liquidus), °C 1080
630
Melting Onset (Solidus), °C 1070
560
Specific Heat Capacity, J/kg-K 380
880
Thermal Conductivity, W/m-K 230
140
Thermal Expansion, µm/m-K 17
22

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 55
30
Electrical Conductivity: Equal Weight (Specific), % IACS 55
95

Otherwise Unclassified Properties

Base Metal Price, % relative 31
10
Density, g/cm3 8.9
2.8
Embodied Carbon, kg CO2/kg material 2.6
7.8
Embodied Energy, MJ/kg 42
150
Embodied Water, L/kg 310
1100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 82
14
Resilience: Unit (Modulus of Resilience), kJ/m3 29
110
Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 18
49
Strength to Weight: Axial, points 8.3
25
Strength to Weight: Bending, points 10
32
Thermal Diffusivity, mm2/s 66
54
Thermal Shock Resistance, points 9.5
12

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
88.4 to 92.9
Copper (Cu), % 98.6 to 99.49
2.6 to 3.6
Iron (Fe), % 0 to 0.050
0 to 0.6
Lead (Pb), % 0 to 0.050
0 to 0.1
Magnesium (Mg), % 0
0 to 0.050
Manganese (Mn), % 0
0 to 0.55
Nickel (Ni), % 0
0 to 0.1
Phosphorus (P), % 0.010 to 0.050
0
Silicon (Si), % 0
4.5 to 6.0
Tin (Sn), % 0.5 to 0.8
0 to 0.050
Titanium (Ti), % 0
0 to 0.25
Zinc (Zn), % 0
0 to 0.2
Residuals, % 0 to 0.5
0 to 0.15