C50100 Bronze vs. Grade 702C Zirconium

C50100 bronze belongs to the copper alloys classification, while grade 702C zirconium belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is C50100 bronze and the bottom bar is grade 702C zirconium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
97
Elongation at Break, % 40
13
Poisson's Ratio 0.34
0.34
Shear Modulus, GPa 43
36
Tensile Strength: Ultimate (UTS), MPa 270
430
Tensile Strength: Yield (Proof), MPa 82
310

Thermal Properties

Latent Heat of Fusion, J/g 210
250
Specific Heat Capacity, J/kg-K 380
270
Thermal Conductivity, W/m-K 230
22
Thermal Expansion, µm/m-K 17
5.7

Otherwise Unclassified Properties

Density, g/cm3 8.9
6.7
Embodied Water, L/kg 310
450

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 82
52
Resilience: Unit (Modulus of Resilience), kJ/m3 29
510
Stiffness to Weight: Axial, points 7.2
8.1
Stiffness to Weight: Bending, points 18
23
Strength to Weight: Axial, points 8.3
18
Strength to Weight: Bending, points 10
19
Thermal Diffusivity, mm2/s 66
12
Thermal Shock Resistance, points 9.5
55

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.1
Copper (Cu), % 98.6 to 99.49
0
Hafnium (Hf), % 0
0 to 4.5
Hydrogen (H), % 0
0 to 0.0050
Iron (Fe), % 0 to 0.050
0 to 0.3
Lead (Pb), % 0 to 0.050
0
Nitrogen (N), % 0
0 to 0.030
Oxygen (O), % 0
0 to 0.25
Phosphorus (P), % 0.010 to 0.050
0 to 0.010
Tin (Sn), % 0.5 to 0.8
0
Zirconium (Zr), % 0
94.8 to 100
Residuals, % 0 to 0.5
0