C50100 Bronze vs. Grade Ti-Pd8A Titanium

C50100 bronze belongs to the copper alloys classification, while grade Ti-Pd8A titanium belongs to the titanium alloys. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is C50100 bronze and the bottom bar is grade Ti-Pd8A titanium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
110
Elongation at Break, % 40
13
Poisson's Ratio 0.34
0.32
Shear Modulus, GPa 43
40
Tensile Strength: Ultimate (UTS), MPa 270
500
Tensile Strength: Yield (Proof), MPa 82
430

Thermal Properties

Latent Heat of Fusion, J/g 210
420
Maximum Temperature: Mechanical, °C 200
320
Melting Completion (Liquidus), °C 1080
1660
Melting Onset (Solidus), °C 1070
1610
Specific Heat Capacity, J/kg-K 380
540
Thermal Conductivity, W/m-K 230
21
Thermal Expansion, µm/m-K 17
8.7

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 55
3.5
Electrical Conductivity: Equal Weight (Specific), % IACS 55
6.9

Otherwise Unclassified Properties

Density, g/cm3 8.9
4.5
Embodied Carbon, kg CO2/kg material 2.6
49
Embodied Energy, MJ/kg 42
840
Embodied Water, L/kg 310
520

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 82
65
Resilience: Unit (Modulus of Resilience), kJ/m3 29
880
Stiffness to Weight: Axial, points 7.2
13
Stiffness to Weight: Bending, points 18
35
Strength to Weight: Axial, points 8.3
31
Strength to Weight: Bending, points 10
31
Thermal Diffusivity, mm2/s 66
8.6
Thermal Shock Resistance, points 9.5
39

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.1
Copper (Cu), % 98.6 to 99.49
0
Hydrogen (H), % 0
0 to 0.015
Iron (Fe), % 0 to 0.050
0 to 0.25
Lead (Pb), % 0 to 0.050
0
Nickel (Ni), % 0
0 to 0.050
Oxygen (O), % 0
0 to 0.4
Palladium (Pd), % 0
0.12 to 0.3
Phosphorus (P), % 0.010 to 0.050
0
Tin (Sn), % 0.5 to 0.8
0
Titanium (Ti), % 0
98.8 to 99.9
Residuals, % 0 to 0.5
0 to 0.4