C50100 Bronze vs. Nickel 908

C50100 bronze belongs to the copper alloys classification, while nickel 908 belongs to the nickel alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is C50100 bronze and the bottom bar is nickel 908.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
180
Elongation at Break, % 40
11
Poisson's Ratio 0.34
0.3
Shear Modulus, GPa 43
70
Shear Strength, MPa 180
800
Tensile Strength: Ultimate (UTS), MPa 270
1340
Tensile Strength: Yield (Proof), MPa 82
930

Thermal Properties

Latent Heat of Fusion, J/g 210
290
Maximum Temperature: Mechanical, °C 200
920
Melting Completion (Liquidus), °C 1080
1430
Melting Onset (Solidus), °C 1070
1380
Specific Heat Capacity, J/kg-K 380
460
Thermal Conductivity, W/m-K 230
11
Thermal Expansion, µm/m-K 17
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 31
50
Density, g/cm3 8.9
8.3
Embodied Carbon, kg CO2/kg material 2.6
9.3
Embodied Energy, MJ/kg 42
140
Embodied Water, L/kg 310
170

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 82
140
Resilience: Unit (Modulus of Resilience), kJ/m3 29
2340
Stiffness to Weight: Axial, points 7.2
12
Stiffness to Weight: Bending, points 18
23
Strength to Weight: Axial, points 8.3
45
Strength to Weight: Bending, points 10
33
Thermal Diffusivity, mm2/s 66
2.9
Thermal Shock Resistance, points 9.5
61

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0.75 to 1.3
Boron (B), % 0
0 to 0.012
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
3.8 to 4.5
Cobalt (Co), % 0
0 to 0.5
Copper (Cu), % 98.6 to 99.49
0 to 0.5
Iron (Fe), % 0 to 0.050
35.6 to 44.6
Lead (Pb), % 0 to 0.050
0
Manganese (Mn), % 0
0 to 1.0
Nickel (Ni), % 0
47 to 51
Niobium (Nb), % 0
2.7 to 3.3
Phosphorus (P), % 0.010 to 0.050
0 to 0.015
Silicon (Si), % 0
0 to 0.5
Sulfur (S), % 0
0 to 0.0050
Tin (Sn), % 0.5 to 0.8
0
Titanium (Ti), % 0
1.2 to 1.8
Residuals, % 0 to 0.5
0