C50100 Bronze vs. SAE-AISI 1137 Steel

C50100 bronze belongs to the copper alloys classification, while SAE-AISI 1137 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is C50100 bronze and the bottom bar is SAE-AISI 1137 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
190
Elongation at Break, % 40
11 to 17
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 43
73
Shear Strength, MPa 180
430 to 460
Tensile Strength: Ultimate (UTS), MPa 270
700 to 760
Tensile Strength: Yield (Proof), MPa 82
370 to 650

Thermal Properties

Latent Heat of Fusion, J/g 210
250
Maximum Temperature: Mechanical, °C 200
400
Melting Completion (Liquidus), °C 1080
1460
Melting Onset (Solidus), °C 1070
1420
Specific Heat Capacity, J/kg-K 380
470
Thermal Conductivity, W/m-K 230
51
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 55
10
Electrical Conductivity: Equal Weight (Specific), % IACS 55
12

Otherwise Unclassified Properties

Base Metal Price, % relative 31
1.9
Density, g/cm3 8.9
7.8
Embodied Carbon, kg CO2/kg material 2.6
1.4
Embodied Energy, MJ/kg 42
19
Embodied Water, L/kg 310
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 82
81 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 29
360 to 1130
Stiffness to Weight: Axial, points 7.2
13
Stiffness to Weight: Bending, points 18
24
Strength to Weight: Axial, points 8.3
25 to 27
Strength to Weight: Bending, points 10
22 to 24
Thermal Diffusivity, mm2/s 66
14
Thermal Shock Resistance, points 9.5
21 to 23

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.32 to 0.39
Copper (Cu), % 98.6 to 99.49
0
Iron (Fe), % 0 to 0.050
97.8 to 98.3
Lead (Pb), % 0 to 0.050
0
Manganese (Mn), % 0
1.4 to 1.7
Phosphorus (P), % 0.010 to 0.050
0 to 0.040
Sulfur (S), % 0
0.080 to 0.13
Tin (Sn), % 0.5 to 0.8
0
Residuals, % 0 to 0.5
0