C50100 Bronze vs. S20910 Stainless Steel

C50100 bronze belongs to the copper alloys classification, while S20910 stainless steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is C50100 bronze and the bottom bar is S20910 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
200
Elongation at Break, % 40
14 to 39
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 43
79
Shear Strength, MPa 180
500 to 570
Tensile Strength: Ultimate (UTS), MPa 270
780 to 940
Tensile Strength: Yield (Proof), MPa 82
430 to 810

Thermal Properties

Latent Heat of Fusion, J/g 210
300
Maximum Temperature: Mechanical, °C 200
1080
Melting Completion (Liquidus), °C 1080
1420
Melting Onset (Solidus), °C 1070
1380
Specific Heat Capacity, J/kg-K 380
480
Thermal Conductivity, W/m-K 230
13
Thermal Expansion, µm/m-K 17
16

Otherwise Unclassified Properties

Base Metal Price, % relative 31
22
Density, g/cm3 8.9
7.8
Embodied Carbon, kg CO2/kg material 2.6
4.8
Embodied Energy, MJ/kg 42
68
Embodied Water, L/kg 310
180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 82
120 to 260
Resilience: Unit (Modulus of Resilience), kJ/m3 29
460 to 1640
Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 18
25
Strength to Weight: Axial, points 8.3
28 to 33
Strength to Weight: Bending, points 10
24 to 27
Thermal Diffusivity, mm2/s 66
3.6
Thermal Shock Resistance, points 9.5
17 to 21

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.060
Chromium (Cr), % 0
20.5 to 23.5
Copper (Cu), % 98.6 to 99.49
0
Iron (Fe), % 0 to 0.050
52.1 to 62.1
Lead (Pb), % 0 to 0.050
0
Manganese (Mn), % 0
4.0 to 6.0
Molybdenum (Mo), % 0
1.5 to 3.0
Nickel (Ni), % 0
11.5 to 13.5
Niobium (Nb), % 0
0.1 to 0.3
Nitrogen (N), % 0
0.2 to 0.4
Phosphorus (P), % 0.010 to 0.050
0 to 0.040
Silicon (Si), % 0
0 to 0.75
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 0.5 to 0.8
0
Vanadium (V), % 0
0.1 to 0.3
Residuals, % 0 to 0.5
0