C51000 Bronze vs. C83600 Ounce Metal
Both C51000 bronze and C83600 ounce metal are copper alloys. They have a moderately high 91% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C51000 bronze and the bottom bar is C83600 ounce metal.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 2.7 to 64 | |
| 21 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 42 | |
| 39 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 780 | |
| 250 |
| Tensile Strength: Yield (Proof), MPa | 130 to 750 | |
| 120 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 160 |
| Melting Completion (Liquidus), °C | 1050 | |
| 1010 |
| Melting Onset (Solidus), °C | 960 | |
| 850 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 370 |
| Thermal Conductivity, W/m-K | 77 | |
| 72 |
| Thermal Expansion, µm/m-K | 18 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 18 | |
| 15 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 18 | |
| 15 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 31 |
| Density, g/cm3 | 8.8 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 3.1 | |
| 3.1 |
| Embodied Energy, MJ/kg | 50 | |
| 50 |
| Embodied Water, L/kg | 350 | |
| 350 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 7.0 to 490 | |
| 43 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 75 to 2490 | |
| 70 |
| Stiffness to Weight: Axial, points | 7.0 | |
| 6.7 |
| Stiffness to Weight: Bending, points | 18 | |
| 18 |
| Strength to Weight: Axial, points | 10 to 25 | |
| 7.9 |
| Strength to Weight: Bending, points | 12 to 21 | |
| 10 |
| Thermal Diffusivity, mm2/s | 23 | |
| 22 |
| Thermal Shock Resistance, points | 12 to 28 | |
| 9.3 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 0 to 0.25 |
| Copper (Cu), % | 92.9 to 95.5 | |
| 84 to 86 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.3 |
| Lead (Pb), % | 0 to 0.050 | |
| 4.0 to 6.0 |
| Nickel (Ni), % | 0 | |
| 0 to 1.0 |
| Phosphorus (P), % | 0.030 to 0.35 | |
| 0 to 1.5 |
| Silicon (Si), % | 0 | |
| 0 to 0.0050 |
| Sulfur (S), % | 0 | |
| 0 to 0.080 |
| Tin (Sn), % | 4.5 to 5.8 | |
| 4.0 to 6.0 |
| Zinc (Zn), % | 0 to 0.3 | |
| 4.0 to 6.0 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.7 |