C51100 Bronze vs. C27200 Brass
Both C51100 bronze and C27200 brass are copper alloys. They have 64% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C51100 bronze and the bottom bar is C27200 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 2.5 to 50 | |
| 10 to 50 |
| Poisson's Ratio | 0.34 | |
| 0.31 |
| Rockwell B Hardness | 67 to 93 | |
| 53 to 86 |
| Shear Modulus, GPa | 42 | |
| 40 |
| Shear Strength, MPa | 230 to 410 | |
| 230 to 320 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 720 | |
| 370 to 590 |
| Tensile Strength: Yield (Proof), MPa | 93 to 700 | |
| 150 to 410 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 130 |
| Melting Completion (Liquidus), °C | 1060 | |
| 920 |
| Melting Onset (Solidus), °C | 970 | |
| 870 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 390 |
| Thermal Conductivity, W/m-K | 84 | |
| 120 |
| Thermal Expansion, µm/m-K | 18 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 20 | |
| 28 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 20 | |
| 31 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 32 | |
| 24 |
| Density, g/cm3 | 8.9 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 2.7 |
| Embodied Energy, MJ/kg | 48 | |
| 45 |
| Embodied Water, L/kg | 340 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 18 to 140 | |
| 30 to 270 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 38 to 2170 | |
| 110 to 810 |
| Stiffness to Weight: Axial, points | 7.1 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 18 | |
| 19 |
| Strength to Weight: Axial, points | 10 to 22 | |
| 13 to 20 |
| Strength to Weight: Bending, points | 12 to 20 | |
| 14 to 19 |
| Thermal Diffusivity, mm2/s | 25 | |
| 37 |
| Thermal Shock Resistance, points | 12 to 26 | |
| 12 to 20 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 93.8 to 96.5 | |
| 62 to 65 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.070 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.070 |
| Phosphorus (P), % | 0.030 to 0.35 | |
| 0 |
| Tin (Sn), % | 3.5 to 4.9 | |
| 0 |
| Zinc (Zn), % | 0 to 0.3 | |
| 34.6 to 38 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.3 |