C51100 Bronze vs. C41500 Brass
Both C51100 bronze and C41500 brass are copper alloys. They have a moderately high 93% of their average alloy composition in common.
For each property being compared, the top bar is C51100 bronze and the bottom bar is C41500 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 2.5 to 50 | |
| 2.0 to 42 |
| Poisson's Ratio | 0.34 | |
| 0.33 |
| Rockwell B Hardness | 67 to 93 | |
| 62 to 90 |
| Rockwell Superficial 30T Hardness | 33 to 79 | |
| 36 to 75 |
| Shear Modulus, GPa | 42 | |
| 42 |
| Shear Strength, MPa | 230 to 410 | |
| 220 to 360 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 720 | |
| 340 to 560 |
| Tensile Strength: Yield (Proof), MPa | 93 to 700 | |
| 190 to 550 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 180 |
| Melting Completion (Liquidus), °C | 1060 | |
| 1030 |
| Melting Onset (Solidus), °C | 970 | |
| 1010 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 380 |
| Thermal Conductivity, W/m-K | 84 | |
| 120 |
| Thermal Expansion, µm/m-K | 18 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 20 | |
| 28 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 20 | |
| 29 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 32 | |
| 30 |
| Density, g/cm3 | 8.9 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 2.8 |
| Embodied Energy, MJ/kg | 48 | |
| 45 |
| Embodied Water, L/kg | 340 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 18 to 140 | |
| 11 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 38 to 2170 | |
| 160 to 1340 |
| Stiffness to Weight: Axial, points | 7.1 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 18 | |
| 18 |
| Strength to Weight: Axial, points | 10 to 22 | |
| 11 to 18 |
| Strength to Weight: Bending, points | 12 to 20 | |
| 12 to 17 |
| Thermal Diffusivity, mm2/s | 25 | |
| 37 |
| Thermal Shock Resistance, points | 12 to 26 | |
| 12 to 20 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 93.8 to 96.5 | |
| 89 to 93 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.1 |
| Phosphorus (P), % | 0.030 to 0.35 | |
| 0 |
| Tin (Sn), % | 3.5 to 4.9 | |
| 1.5 to 2.2 |
| Zinc (Zn), % | 0 to 0.3 | |
| 4.2 to 9.5 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.5 |