C51900 Bronze vs. S17600 Stainless Steel
C51900 bronze belongs to the copper alloys classification, while S17600 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is C51900 bronze and the bottom bar is S17600 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 200 |
| Elongation at Break, % | 14 to 29 | |
| 8.6 to 11 |
| Poisson's Ratio | 0.34 | |
| 0.28 |
| Shear Modulus, GPa | 42 | |
| 76 |
| Shear Strength, MPa | 320 to 370 | |
| 560 to 880 |
| Tensile Strength: Ultimate (UTS), MPa | 380 to 620 | |
| 940 to 1490 |
| Tensile Strength: Yield (Proof), MPa | 390 to 570 | |
| 580 to 1310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 890 |
| Melting Completion (Liquidus), °C | 1040 | |
| 1430 |
| Melting Onset (Solidus), °C | 930 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 480 |
| Thermal Conductivity, W/m-K | 66 | |
| 15 |
| Thermal Expansion, µm/m-K | 18 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 14 | |
| 2.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 14 | |
| 2.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 13 |
| Density, g/cm3 | 8.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 3.2 | |
| 2.9 |
| Embodied Energy, MJ/kg | 51 | |
| 42 |
| Embodied Water, L/kg | 360 | |
| 130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 55 to 180 | |
| 70 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 680 to 1450 | |
| 850 to 4390 |
| Stiffness to Weight: Axial, points | 7.0 | |
| 14 |
| Stiffness to Weight: Bending, points | 18 | |
| 25 |
| Strength to Weight: Axial, points | 12 to 19 | |
| 34 to 54 |
| Strength to Weight: Bending, points | 13 to 18 | |
| 28 to 37 |
| Thermal Diffusivity, mm2/s | 20 | |
| 4.1 |
| Thermal Shock Resistance, points | 14 to 22 | |
| 31 to 50 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 0.4 |
| Carbon (C), % | 0 | |
| 0 to 0.080 |
| Chromium (Cr), % | 0 | |
| 16 to 17.5 |
| Copper (Cu), % | 91.7 to 95 | |
| 0 |
| Iron (Fe), % | 0 to 0.1 | |
| 71.3 to 77.6 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 | |
| 6.0 to 7.5 |
| Phosphorus (P), % | 0.030 to 0.35 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tin (Sn), % | 5.0 to 7.0 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0.4 to 1.2 |
| Zinc (Zn), % | 0 to 0.3 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |