C55280 Copper vs. AWS BNi-2
C55280 copper belongs to the copper alloys classification, while AWS BNi-2 belongs to the nickel alloys. There are 18 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C55280 copper and the bottom bar is AWS BNi-2.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 180 |
| Poisson's Ratio | 0.34 | |
| 0.3 |
| Shear Modulus, GPa | 40 | |
| 68 |
| Tensile Strength: Ultimate (UTS), MPa | 180 | |
| 440 |
Thermal Properties
| Brazing Temperature, °C | 730 to 820 | |
| 1010 to 1180 |
| Latent Heat of Fusion, J/g | 190 | |
| 360 |
| Melting Completion (Liquidus), °C | 790 | |
| 1000 |
| Melting Onset (Solidus), °C | 640 | |
| 970 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 490 |
| Thermal Expansion, µm/m-K | 16 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.5 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 4.2 | |
| 9.3 |
| Embodied Energy, MJ/kg | 67 | |
| 130 |
Common Calculations
| Stiffness to Weight: Axial, points | 6.9 | |
| 12 |
| Stiffness to Weight: Bending, points | 19 | |
| 23 |
| Strength to Weight: Axial, points | 5.9 | |
| 15 |
| Strength to Weight: Bending, points | 8.3 | |
| 16 |
| Thermal Shock Resistance, points | 7.4 | |
| 16 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 0.050 |
| Boron (B), % | 0 | |
| 2.8 to 3.5 |
| Carbon (C), % | 0 | |
| 0 to 0.060 |
| Chromium (Cr), % | 0 | |
| 6.0 to 8.0 |
| Cobalt (Co), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 90.5 to 91.4 | |
| 0 |
| Iron (Fe), % | 0 | |
| 2.5 to 3.5 |
| Nickel (Ni), % | 0 | |
| 79.1 to 84.8 |
| Phosphorus (P), % | 6.8 to 7.2 | |
| 0 to 0.020 |
| Selenium (Se), % | 0 | |
| 0 to 0.0050 |
| Silicon (Si), % | 0 | |
| 4.0 to 5.0 |
| Silver (Ag), % | 1.8 to 2.2 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.020 |
| Titanium (Ti), % | 0 | |
| 0 to 0.050 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.050 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.5 |