MakeItFrom.com
Menu (ESC)

C55282 Copper vs. CC332G Bronze

Both C55282 copper and CC332G bronze are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 83% of their average alloy composition in common. There are 18 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is C55282 copper and the bottom bar is CC332G bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
120
Poisson's Ratio 0.34
0.34
Shear Modulus, GPa 39
43
Tensile Strength: Ultimate (UTS), MPa 180
620

Thermal Properties

Latent Heat of Fusion, J/g 190
230
Maximum Temperature: Mechanical, °C 200
220
Melting Completion (Liquidus), °C 770
1060
Melting Onset (Solidus), °C 640
1010
Specific Heat Capacity, J/kg-K 400
440
Thermal Expansion, µm/m-K 16
18

Otherwise Unclassified Properties

Density, g/cm3 8.6
8.3
Embodied Carbon, kg CO2/kg material 7.0
3.4
Embodied Energy, MJ/kg 110
55

Common Calculations

Stiffness to Weight: Axial, points 6.8
7.7
Stiffness to Weight: Bending, points 18
20
Strength to Weight: Axial, points 5.8
21
Strength to Weight: Bending, points 8.2
19
Thermal Shock Resistance, points 7.4
21

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
8.5 to 10.5
Copper (Cu), % 87.7 to 88.7
80 to 86
Iron (Fe), % 0
1.0 to 3.0
Lead (Pb), % 0
0 to 0.1
Magnesium (Mg), % 0
0 to 0.050
Manganese (Mn), % 0
0 to 2.0
Nickel (Ni), % 0
1.5 to 4.0
Phosphorus (P), % 6.5 to 7.0
0
Silicon (Si), % 0
0 to 0.2
Silver (Ag), % 4.8 to 5.2
0
Tin (Sn), % 0
0 to 0.2
Zinc (Zn), % 0
0 to 0.5
Residuals, % 0 to 0.15
0