C55282 Copper vs. CC754S Brass

Both C55282 copper and CC754S brass are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 60% of their average alloy composition in common. There are 18 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is C55282 copper and the bottom bar is CC754S brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
100
Poisson's Ratio 0.34
0.31
Shear Modulus, GPa 39
40
Tensile Strength: Ultimate (UTS), MPa 180
320

Thermal Properties

Latent Heat of Fusion, J/g 190
170
Maximum Temperature: Mechanical, °C 200
120
Melting Completion (Liquidus), °C 770
830
Melting Onset (Solidus), °C 640
780
Specific Heat Capacity, J/kg-K 400
390
Thermal Expansion, µm/m-K 16
21

Otherwise Unclassified Properties

Density, g/cm3 8.6
8.1
Embodied Carbon, kg CO2/kg material 7.0
2.8
Embodied Energy, MJ/kg 110
47

Common Calculations

Stiffness to Weight: Axial, points 6.8
7.2
Stiffness to Weight: Bending, points 18
19
Strength to Weight: Axial, points 5.8
11
Strength to Weight: Bending, points 8.2
13
Thermal Shock Resistance, points 7.4
10

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.8
Copper (Cu), % 87.7 to 88.7
57 to 63
Iron (Fe), % 0
0 to 0.7
Lead (Pb), % 0
0.5 to 2.5
Manganese (Mn), % 0
0 to 0.5
Nickel (Ni), % 0
0 to 1.0
Phosphorus (P), % 6.5 to 7.0
0 to 0.020
Silicon (Si), % 0
0 to 0.3
Silver (Ag), % 4.8 to 5.2
0
Tin (Sn), % 0
0 to 1.0
Zinc (Zn), % 0
30.2 to 42.5
Residuals, % 0 to 0.15
0