C55282 Copper vs. C10700 Copper

Both C55282 copper and C10700 copper are copper alloys. They have 88% of their average alloy composition in common. There are 18 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is C55282 copper and the bottom bar is C10700 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
120
Poisson's Ratio 0.34
0.34
Shear Modulus, GPa 39
43
Tensile Strength: Ultimate (UTS), MPa 180
230 to 410

Thermal Properties

Latent Heat of Fusion, J/g 190
210
Maximum Temperature: Mechanical, °C 200
200
Melting Completion (Liquidus), °C 770
1080
Melting Onset (Solidus), °C 640
1080
Specific Heat Capacity, J/kg-K 400
390
Thermal Expansion, µm/m-K 16
17

Otherwise Unclassified Properties

Density, g/cm3 8.6
9.0
Embodied Carbon, kg CO2/kg material 7.0
2.7
Embodied Energy, MJ/kg 110
42

Common Calculations

Stiffness to Weight: Axial, points 6.8
7.2
Stiffness to Weight: Bending, points 18
18
Strength to Weight: Axial, points 5.8
7.2 to 13
Strength to Weight: Bending, points 8.2
9.4 to 14
Thermal Shock Resistance, points 7.4
8.2 to 15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 87.7 to 88.7
99.83 to 99.915
Oxygen (O), % 0
0 to 0.0010
Phosphorus (P), % 6.5 to 7.0
0
Silver (Ag), % 4.8 to 5.2
0.085 to 0.12
Residuals, % 0 to 0.15
0 to 0.050