C55282 Copper vs. C67400 Bronze

Both C55282 copper and C67400 bronze are copper alloys. They have 59% of their average alloy composition in common. There are 18 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is C55282 copper and the bottom bar is C67400 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
110
Poisson's Ratio 0.34
0.31
Shear Modulus, GPa 39
41
Tensile Strength: Ultimate (UTS), MPa 180
480 to 610

Thermal Properties

Latent Heat of Fusion, J/g 190
190
Maximum Temperature: Mechanical, °C 200
130
Melting Completion (Liquidus), °C 770
890
Melting Onset (Solidus), °C 640
870
Specific Heat Capacity, J/kg-K 400
400
Thermal Expansion, µm/m-K 16
21

Otherwise Unclassified Properties

Density, g/cm3 8.6
7.9
Embodied Carbon, kg CO2/kg material 7.0
2.8
Embodied Energy, MJ/kg 110
48

Common Calculations

Stiffness to Weight: Axial, points 6.8
7.5
Stiffness to Weight: Bending, points 18
20
Strength to Weight: Axial, points 5.8
17 to 22
Strength to Weight: Bending, points 8.2
17 to 20
Thermal Shock Resistance, points 7.4
16 to 20

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0.5 to 2.0
Copper (Cu), % 87.7 to 88.7
57 to 60
Iron (Fe), % 0
0 to 0.35
Lead (Pb), % 0
0 to 0.5
Manganese (Mn), % 0
2.0 to 3.5
Nickel (Ni), % 0
0 to 0.25
Phosphorus (P), % 6.5 to 7.0
0
Silicon (Si), % 0
0.5 to 1.5
Silver (Ag), % 4.8 to 5.2
0
Tin (Sn), % 0
0 to 0.3
Zinc (Zn), % 0
31.1 to 40
Residuals, % 0 to 0.15
0 to 0.5