C55282 Copper vs. C90200 Bronze

Both C55282 copper and C90200 bronze are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 88% of their average alloy composition in common. There are 18 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is C55282 copper and the bottom bar is C90200 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
110
Poisson's Ratio 0.34
0.34
Shear Modulus, GPa 39
41
Tensile Strength: Ultimate (UTS), MPa 180
260

Thermal Properties

Latent Heat of Fusion, J/g 190
200
Maximum Temperature: Mechanical, °C 200
180
Melting Completion (Liquidus), °C 770
1050
Melting Onset (Solidus), °C 640
880
Specific Heat Capacity, J/kg-K 400
370
Thermal Expansion, µm/m-K 16
18

Otherwise Unclassified Properties

Density, g/cm3 8.6
8.8
Embodied Carbon, kg CO2/kg material 7.0
3.3
Embodied Energy, MJ/kg 110
53

Common Calculations

Stiffness to Weight: Axial, points 6.8
7.0
Stiffness to Weight: Bending, points 18
18
Strength to Weight: Axial, points 5.8
8.3
Strength to Weight: Bending, points 8.2
10
Thermal Shock Resistance, points 7.4
9.5

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
0 to 0.2
Copper (Cu), % 87.7 to 88.7
91 to 94
Iron (Fe), % 0
0 to 0.2
Lead (Pb), % 0
0 to 0.3
Nickel (Ni), % 0
0 to 0.5
Phosphorus (P), % 6.5 to 7.0
0 to 0.050
Silicon (Si), % 0
0 to 0.0050
Silver (Ag), % 4.8 to 5.2
0
Sulfur (S), % 0
0 to 0.050
Tin (Sn), % 0
6.0 to 8.0
Zinc (Zn), % 0
0 to 0.5
Residuals, % 0 to 0.15
0 to 0.6