C55284 Copper vs. AWS ENiCrFe-2
C55284 copper belongs to the copper alloys classification, while AWS ENiCrFe-2 belongs to the nickel alloys. There are 17 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C55284 copper and the bottom bar is AWS ENiCrFe-2.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 190 |
| Poisson's Ratio | 0.34 | |
| 0.3 |
| Shear Modulus, GPa | 38 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 180 | |
| 790 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 310 |
| Melting Completion (Liquidus), °C | 800 | |
| 1390 |
| Melting Onset (Solidus), °C | 640 | |
| 1350 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 450 |
| Thermal Expansion, µm/m-K | 17 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.9 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 16 | |
| 11 |
| Embodied Energy, MJ/kg | 260 | |
| 160 |
Common Calculations
| Stiffness to Weight: Axial, points | 6.5 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 23 |
| Strength to Weight: Axial, points | 5.6 | |
| 26 |
| Strength to Weight: Bending, points | 8.0 | |
| 22 |
| Thermal Shock Resistance, points | 7.4 | |
| 24 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Chromium (Cr), % | 0 | |
| 13 to 17 |
| Cobalt (Co), % | 0 | |
| 0 to 0.12 |
| Copper (Cu), % | 79.2 to 80.7 | |
| 0 to 0.5 |
| Iron (Fe), % | 0 | |
| 0 to 12 |
| Manganese (Mn), % | 0 | |
| 1.0 to 3.5 |
| Molybdenum (Mo), % | 0 | |
| 0.5 to 2.5 |
| Nickel (Ni), % | 0 | |
| 62 to 85 |
| Niobium (Nb), % | 0 | |
| 0.5 to 4.0 |
| Phosphorus (P), % | 4.8 to 5.2 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0 to 0.75 |
| Silver (Ag), % | 14.5 to 15.5 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.020 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.5 |