C55284 Copper vs. K94200 Alloy
C55284 copper belongs to the copper alloys classification, while K94200 alloy belongs to the iron alloys. There are 13 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is C55284 copper and the bottom bar is K94200 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 140 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 38 | |
| 54 |
| Tensile Strength: Ultimate (UTS), MPa | 180 | |
| 500 to 710 |
Thermal Properties
| Melting Onset (Solidus), °C | 640 | |
| 1440 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 500 |
| Thermal Expansion, µm/m-K | 17 | |
| 5.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.9 | |
| 8.2 |
Common Calculations
| Stiffness to Weight: Axial, points | 6.5 | |
| 9.8 |
| Stiffness to Weight: Bending, points | 18 | |
| 21 |
| Strength to Weight: Axial, points | 5.6 | |
| 17 to 24 |
| Strength to Weight: Bending, points | 8.0 | |
| 17 to 22 |
| Thermal Shock Resistance, points | 7.4 | |
| 49 to 70 |