C60800 Bronze vs. EN 1.0434 Steel
C60800 bronze belongs to the copper alloys classification, while EN 1.0434 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C60800 bronze and the bottom bar is EN 1.0434 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Elongation at Break, % | 55 | |
| 12 to 28 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 46 | |
| 73 |
| Shear Strength, MPa | 290 | |
| 280 to 330 |
| Tensile Strength: Ultimate (UTS), MPa | 390 | |
| 390 to 540 |
| Tensile Strength: Yield (Proof), MPa | 150 | |
| 250 to 450 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 400 |
| Melting Completion (Liquidus), °C | 1060 | |
| 1460 |
| Melting Onset (Solidus), °C | 1050 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 470 |
| Thermal Conductivity, W/m-K | 80 | |
| 52 |
| Thermal Expansion, µm/m-K | 18 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 17 | |
| 7.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 18 | |
| 8.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 1.8 |
| Density, g/cm3 | 8.6 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 1.4 |
| Embodied Energy, MJ/kg | 48 | |
| 18 |
| Embodied Water, L/kg | 360 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 170 | |
| 39 to 140 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 94 | |
| 170 to 540 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 |
| Strength to Weight: Axial, points | 13 | |
| 14 to 19 |
| Strength to Weight: Bending, points | 14 | |
| 15 to 19 |
| Thermal Diffusivity, mm2/s | 23 | |
| 14 |
| Thermal Shock Resistance, points | 14 | |
| 12 to 17 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 5.0 to 6.5 | |
| 0.020 to 0.060 |
| Arsenic (As), % | 0.020 to 0.35 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.15 to 0.19 |
| Copper (Cu), % | 92.5 to 95 | |
| 0 |
| Iron (Fe), % | 0 to 0.1 | |
| 98.8 to 99.18 |
| Lead (Pb), % | 0 to 0.1 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.65 to 0.85 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 | |
| 0 to 0.025 |
| Residuals, % | 0 to 0.5 | |
| 0 |