C60800 Bronze vs. Solder Alloy 121
C60800 bronze belongs to the copper alloys classification, while solder alloy 121 belongs to the otherwise unclassified metals. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is C60800 bronze and the bottom bar is solder alloy 121.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 21 |
| Elongation at Break, % | 55 | |
| 25 |
| Poisson's Ratio | 0.34 | |
| 0.43 |
| Shear Modulus, GPa | 46 | |
| 7.5 |
| Tensile Strength: Ultimate (UTS), MPa | 390 | |
| 32 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 29 |
| Melting Completion (Liquidus), °C | 1060 | |
| 290 |
| Melting Onset (Solidus), °C | 1050 | |
| 230 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 140 |
| Thermal Conductivity, W/m-K | 80 | |
| 31 |
| Thermal Expansion, µm/m-K | 18 | |
| 28 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 17 | |
| 8.8 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 18 | |
| 7.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 80 |
| Density, g/cm3 | 8.6 | |
| 11 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 5.6 |
| Embodied Energy, MJ/kg | 48 | |
| 93 |
| Embodied Water, L/kg | 360 | |
| 580 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.3 | |
| 1.1 |
| Stiffness to Weight: Bending, points | 19 | |
| 8.6 |
| Strength to Weight: Axial, points | 13 | |
| 0.84 |
| Strength to Weight: Bending, points | 14 | |
| 2.1 |
| Thermal Diffusivity, mm2/s | 23 | |
| 20 |
| Thermal Shock Resistance, points | 14 | |
| 3.9 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 5.0 to 6.5 | |
| 0 to 0.0010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.5 |
| Arsenic (As), % | 0.020 to 0.35 | |
| 0 to 0.030 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.25 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0050 |
| Copper (Cu), % | 92.5 to 95 | |
| 0 to 0.080 |
| Gold (Au), % | 0 | |
| 0 to 0.050 |
| Indium (In), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.020 |
| Lead (Pb), % | 0 to 0.1 | |
| 83.4 to 85.5 |
| Nickel (Ni), % | 0 | |
| 0 to 0.010 |
| Silver (Ag), % | 0 | |
| 0 to 0.1 |
| Tin (Sn), % | 0 | |
| 14.5 to 15.5 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0010 |
| Residuals, % | 0 to 0.5 | |
| 0 |