C61300 Bronze vs. C69710 Brass
Both C61300 bronze and C69710 brass are copper alloys. They have 78% of their average alloy composition in common.
For each property being compared, the top bar is C61300 bronze and the bottom bar is C69710 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 34 to 40 | |
| 25 |
| Poisson's Ratio | 0.34 | |
| 0.32 |
| Shear Modulus, GPa | 43 | |
| 41 |
| Shear Strength, MPa | 370 to 390 | |
| 300 |
| Tensile Strength: Ultimate (UTS), MPa | 550 to 580 | |
| 470 |
| Tensile Strength: Yield (Proof), MPa | 230 to 310 | |
| 230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 240 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 160 |
| Melting Completion (Liquidus), °C | 1050 | |
| 930 |
| Melting Onset (Solidus), °C | 1040 | |
| 880 |
| Specific Heat Capacity, J/kg-K | 420 | |
| 400 |
| Thermal Conductivity, W/m-K | 55 | |
| 40 |
| Thermal Expansion, µm/m-K | 18 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 12 | |
| 8.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 13 | |
| 8.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 26 |
| Density, g/cm3 | 8.5 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 2.7 |
| Embodied Energy, MJ/kg | 49 | |
| 44 |
| Embodied Water, L/kg | 370 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 to 190 | |
| 99 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 230 to 410 | |
| 250 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 18 to 19 | |
| 16 |
| Strength to Weight: Bending, points | 18 | |
| 16 |
| Thermal Diffusivity, mm2/s | 15 | |
| 12 |
| Thermal Shock Resistance, points | 19 to 20 | |
| 16 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 6.0 to 7.5 | |
| 0 |
| Arsenic (As), % | 0 | |
| 0.030 to 0.060 |
| Copper (Cu), % | 88 to 91.8 | |
| 75 to 80 |
| Iron (Fe), % | 2.0 to 3.0 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 to 0.010 | |
| 0.5 to 1.5 |
| Manganese (Mn), % | 0 to 0.2 | |
| 0 to 0.4 |
| Nickel (Ni), % | 0 to 0.15 | |
| 0 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 2.5 to 3.5 |
| Tin (Sn), % | 0.2 to 0.5 | |
| 0 |
| Zinc (Zn), % | 0 to 0.2 | |
| 13.8 to 22 |
| Residuals, % | 0 to 0.2 | |
| 0 to 0.5 |