C61500 Bronze vs. EN 2.4878 Nickel
C61500 bronze belongs to the copper alloys classification, while EN 2.4878 nickel belongs to the nickel alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C61500 bronze and the bottom bar is EN 2.4878 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 200 |
| Elongation at Break, % | 3.0 to 55 | |
| 13 to 17 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 42 | |
| 78 |
| Shear Strength, MPa | 350 to 550 | |
| 750 to 760 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 970 | |
| 1210 to 1250 |
| Tensile Strength: Yield (Proof), MPa | 150 to 720 | |
| 740 to 780 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 330 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 1030 |
| Melting Completion (Liquidus), °C | 1040 | |
| 1370 |
| Melting Onset (Solidus), °C | 1030 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 430 | |
| 460 |
| Thermal Conductivity, W/m-K | 58 | |
| 11 |
| Thermal Expansion, µm/m-K | 18 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 80 |
| Density, g/cm3 | 8.4 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 3.2 | |
| 10 |
| Embodied Energy, MJ/kg | 52 | |
| 150 |
| Embodied Water, L/kg | 380 | |
| 370 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 27 to 200 | |
| 150 to 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 100 to 2310 | |
| 1370 to 1540 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 |
| Strength to Weight: Axial, points | 16 to 32 | |
| 41 to 42 |
| Strength to Weight: Bending, points | 16 to 26 | |
| 31 |
| Thermal Diffusivity, mm2/s | 16 | |
| 2.8 |
| Thermal Shock Resistance, points | 17 to 34 | |
| 37 to 39 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 7.7 to 8.3 | |
| 1.2 to 1.6 |
| Boron (B), % | 0 | |
| 0.010 to 0.015 |
| Carbon (C), % | 0 | |
| 0.030 to 0.070 |
| Chromium (Cr), % | 0 | |
| 23 to 25 |
| Cobalt (Co), % | 0 | |
| 19 to 21 |
| Copper (Cu), % | 89 to 90.5 | |
| 0 to 0.2 |
| Iron (Fe), % | 0 | |
| 0 to 1.0 |
| Lead (Pb), % | 0 to 0.015 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0 | |
| 1.0 to 2.0 |
| Nickel (Ni), % | 1.8 to 2.2 | |
| 43.6 to 52.2 |
| Niobium (Nb), % | 0 | |
| 0.7 to 1.2 |
| Phosphorus (P), % | 0 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.0070 |
| Tantalum (Ta), % | 0 | |
| 0 to 0.050 |
| Titanium (Ti), % | 0 | |
| 2.8 to 3.2 |
| Zirconium (Zr), % | 0 | |
| 0.030 to 0.070 |
| Residuals, % | 0 to 0.5 | |
| 0 |