C62400 Bronze vs. Nickel 80A
C62400 bronze belongs to the copper alloys classification, while nickel 80A belongs to the nickel alloys. There are 29 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C62400 bronze and the bottom bar is nickel 80A.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Elongation at Break, % | 11 to 14 | |
| 22 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 42 | |
| 74 |
| Shear Strength, MPa | 420 to 440 | |
| 660 |
| Tensile Strength: Ultimate (UTS), MPa | 690 to 730 | |
| 1040 |
| Tensile Strength: Yield (Proof), MPa | 270 to 350 | |
| 710 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 980 |
| Melting Completion (Liquidus), °C | 1040 | |
| 1360 |
| Melting Onset (Solidus), °C | 1030 | |
| 1310 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 470 |
| Thermal Conductivity, W/m-K | 59 | |
| 11 |
| Thermal Expansion, µm/m-K | 18 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 12 | |
| 1.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 13 | |
| 1.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 27 | |
| 55 |
| Density, g/cm3 | 8.2 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 3.2 | |
| 9.8 |
| Embodied Energy, MJ/kg | 53 | |
| 140 |
| Embodied Water, L/kg | 400 | |
| 280 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 68 to 77 | |
| 210 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 320 to 550 | |
| 1300 |
| Stiffness to Weight: Axial, points | 7.6 | |
| 13 |
| Stiffness to Weight: Bending, points | 20 | |
| 23 |
| Strength to Weight: Axial, points | 23 to 25 | |
| 35 |
| Strength to Weight: Bending, points | 21 to 22 | |
| 27 |
| Thermal Diffusivity, mm2/s | 16 | |
| 2.9 |
| Thermal Shock Resistance, points | 25 to 26 | |
| 31 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 10 to 11.5 | |
| 0.5 to 1.8 |
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Chromium (Cr), % | 0 | |
| 18 to 21 |
| Copper (Cu), % | 82.8 to 88 | |
| 0 |
| Iron (Fe), % | 2.0 to 4.5 | |
| 0 to 3.0 |
| Manganese (Mn), % | 0 to 0.3 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 | |
| 69.4 to 79.7 |
| Silicon (Si), % | 0 to 0.25 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Tin (Sn), % | 0 to 0.2 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 1.8 to 2.7 |
| Residuals, % | 0 to 0.5 | |
| 0 |