C62400 Bronze vs. C55181 Copper
Both C62400 bronze and C55181 copper are copper alloys. They have 85% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is C62400 bronze and the bottom bar is C55181 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 42 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 690 to 730 | |
| 200 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 200 |
| Melting Completion (Liquidus), °C | 1040 | |
| 790 |
| Melting Onset (Solidus), °C | 1030 | |
| 710 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 410 |
| Thermal Expansion, µm/m-K | 18 | |
| 16 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 27 | |
| 28 |
| Density, g/cm3 | 8.2 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 3.2 | |
| 2.4 |
| Embodied Energy, MJ/kg | 53 | |
| 38 |
| Embodied Water, L/kg | 400 | |
| 290 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.6 | |
| 7.0 |
| Stiffness to Weight: Bending, points | 20 | |
| 19 |
| Strength to Weight: Axial, points | 23 to 25 | |
| 6.5 |
| Strength to Weight: Bending, points | 21 to 22 | |
| 8.9 |
| Thermal Shock Resistance, points | 25 to 26 | |
| 8.2 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 10 to 11.5 | |
| 0 |
| Copper (Cu), % | 82.8 to 88 | |
| 92.4 to 93 |
| Iron (Fe), % | 2.0 to 4.5 | |
| 0 |
| Manganese (Mn), % | 0 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 7.0 to 7.5 |
| Silicon (Si), % | 0 to 0.25 | |
| 0 |
| Tin (Sn), % | 0 to 0.2 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.15 |