C63020 Bronze vs. C10500 Copper

Both C63020 bronze and C10500 copper are copper alloys. They have 78% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is C63020 bronze and the bottom bar is C10500 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
120
Elongation at Break, % 6.8
2.8 to 51
Poisson's Ratio 0.33
0.34
Shear Modulus, GPa 44
43
Shear Strength, MPa 600
150 to 210
Tensile Strength: Ultimate (UTS), MPa 1020
220 to 400
Tensile Strength: Yield (Proof), MPa 740
75 to 400

Thermal Properties

Latent Heat of Fusion, J/g 230
210
Maximum Temperature: Mechanical, °C 230
200
Melting Completion (Liquidus), °C 1070
1080
Melting Onset (Solidus), °C 1020
1080
Specific Heat Capacity, J/kg-K 450
390
Thermal Conductivity, W/m-K 40
390
Thermal Expansion, µm/m-K 18
17

Otherwise Unclassified Properties

Base Metal Price, % relative 29
32
Density, g/cm3 8.2
9.0
Embodied Carbon, kg CO2/kg material 3.6
2.6
Embodied Energy, MJ/kg 58
42
Embodied Water, L/kg 390
350

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 63
11 to 90
Resilience: Unit (Modulus of Resilience), kJ/m3 2320
24 to 680
Stiffness to Weight: Axial, points 8.0
7.2
Stiffness to Weight: Bending, points 20
18
Strength to Weight: Axial, points 34
6.8 to 12
Strength to Weight: Bending, points 27
9.1 to 14
Thermal Diffusivity, mm2/s 11
110
Thermal Shock Resistance, points 35
7.8 to 14

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 10 to 11
0
Chromium (Cr), % 0 to 0.050
0
Cobalt (Co), % 0 to 0.2
0
Copper (Cu), % 74.7 to 81.8
99.89 to 99.966
Iron (Fe), % 4.0 to 5.5
0
Lead (Pb), % 0 to 0.030
0
Manganese (Mn), % 0 to 1.5
0
Nickel (Ni), % 4.2 to 6.0
0
Oxygen (O), % 0
0 to 0.0010
Silver (Ag), % 0
0.034 to 0.060
Tin (Sn), % 0 to 0.25
0
Zinc (Zn), % 0 to 0.3
0
Residuals, % 0 to 0.5
0 to 0.050