C63020 Bronze vs. C10700 Copper

Both C63020 bronze and C10700 copper are copper alloys. They have 78% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is C63020 bronze and the bottom bar is C10700 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
120
Elongation at Break, % 6.8
2.2 to 50
Poisson's Ratio 0.33
0.34
Shear Modulus, GPa 44
43
Shear Strength, MPa 600
160 to 240
Tensile Strength: Ultimate (UTS), MPa 1020
230 to 410
Tensile Strength: Yield (Proof), MPa 740
77 to 410

Thermal Properties

Latent Heat of Fusion, J/g 230
210
Maximum Temperature: Mechanical, °C 230
200
Melting Completion (Liquidus), °C 1070
1080
Melting Onset (Solidus), °C 1020
1080
Specific Heat Capacity, J/kg-K 450
390
Thermal Conductivity, W/m-K 40
390
Thermal Expansion, µm/m-K 18
17

Otherwise Unclassified Properties

Base Metal Price, % relative 29
35
Density, g/cm3 8.2
9.0
Embodied Carbon, kg CO2/kg material 3.6
2.7
Embodied Energy, MJ/kg 58
42
Embodied Water, L/kg 390
390

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 63
7.9 to 91
Resilience: Unit (Modulus of Resilience), kJ/m3 2320
25 to 710
Stiffness to Weight: Axial, points 8.0
7.2
Stiffness to Weight: Bending, points 20
18
Strength to Weight: Axial, points 34
7.2 to 13
Strength to Weight: Bending, points 27
9.4 to 14
Thermal Diffusivity, mm2/s 11
110
Thermal Shock Resistance, points 35
8.2 to 15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 10 to 11
0
Chromium (Cr), % 0 to 0.050
0
Cobalt (Co), % 0 to 0.2
0
Copper (Cu), % 74.7 to 81.8
99.83 to 99.915
Iron (Fe), % 4.0 to 5.5
0
Lead (Pb), % 0 to 0.030
0
Manganese (Mn), % 0 to 1.5
0
Nickel (Ni), % 4.2 to 6.0
0
Oxygen (O), % 0
0 to 0.0010
Silver (Ag), % 0
0.085 to 0.12
Tin (Sn), % 0 to 0.25
0
Zinc (Zn), % 0 to 0.3
0
Residuals, % 0 to 0.5
0 to 0.050