C63020 Bronze vs. C77600 Nickel Silver
Both C63020 bronze and C77600 nickel silver are copper alloys. They have 49% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C63020 bronze and the bottom bar is C77600 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Elongation at Break, % | 6.8 | |
| 30 |
| Poisson's Ratio | 0.33 | |
| 0.3 |
| Shear Modulus, GPa | 44 | |
| 43 |
| Shear Strength, MPa | 600 | |
| 410 |
| Tensile Strength: Ultimate (UTS), MPa | 1020 | |
| 630 |
| Tensile Strength: Yield (Proof), MPa | 740 | |
| 320 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 180 |
| Maximum Temperature: Mechanical, °C | 230 | |
| 140 |
| Melting Completion (Liquidus), °C | 1070 | |
| 830 |
| Melting Onset (Solidus), °C | 1020 | |
| 790 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 390 |
| Thermal Expansion, µm/m-K | 18 | |
| 20 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 27 |
| Density, g/cm3 | 8.2 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 3.6 | |
| 3.7 |
| Embodied Energy, MJ/kg | 58 | |
| 60 |
| Embodied Water, L/kg | 390 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 63 | |
| 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2320 | |
| 470 |
| Stiffness to Weight: Axial, points | 8.0 | |
| 7.9 |
| Stiffness to Weight: Bending, points | 20 | |
| 20 |
| Strength to Weight: Axial, points | 34 | |
| 22 |
| Strength to Weight: Bending, points | 27 | |
| 21 |
| Thermal Shock Resistance, points | 35 | |
| 20 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 10 to 11 | |
| 0 |
| Chromium (Cr), % | 0 to 0.050 | |
| 0 |
| Cobalt (Co), % | 0 to 0.2 | |
| 0 |
| Copper (Cu), % | 74.7 to 81.8 | |
| 42 to 45 |
| Iron (Fe), % | 4.0 to 5.5 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 to 0.030 | |
| 0 to 0.25 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0 to 0.25 |
| Nickel (Ni), % | 4.2 to 6.0 | |
| 12 to 14 |
| Tin (Sn), % | 0 to 0.25 | |
| 0 to 0.15 |
| Zinc (Zn), % | 0 to 0.3 | |
| 39.7 to 46 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.5 |