C63200 Bronze vs. Grade 361 Molybdenum
C63200 bronze belongs to the copper alloys classification, while grade 361 molybdenum belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is C63200 bronze and the bottom bar is grade 361 molybdenum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 310 |
| Elongation at Break, % | 17 to 18 | |
| 6.3 |
| Poisson's Ratio | 0.34 | |
| 0.31 |
| Shear Modulus, GPa | 44 | |
| 120 |
| Tensile Strength: Ultimate (UTS), MPa | 640 to 710 | |
| 620 |
| Tensile Strength: Yield (Proof), MPa | 310 to 350 | |
| 530 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 370 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 250 |
| Thermal Expansion, µm/m-K | 18 | |
| 7.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.3 | |
| 10 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 28 |
| Embodied Energy, MJ/kg | 55 | |
| 330 |
| Embodied Water, L/kg | 380 | |
| 360 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 95 to 99 | |
| 37 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 400 to 510 | |
| 450 |
| Stiffness to Weight: Axial, points | 7.9 | |
| 17 |
| Stiffness to Weight: Bending, points | 20 | |
| 22 |
| Strength to Weight: Axial, points | 21 to 24 | |
| 17 |
| Strength to Weight: Bending, points | 20 to 21 | |
| 16 |
| Thermal Shock Resistance, points | 22 to 24 | |
| 21 |
Alloy Composition
| Aluminum (Al), % | 8.7 to 9.5 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.010 |
| Copper (Cu), % | 78.8 to 82.6 | |
| 0 |
| Iron (Fe), % | 3.5 to 4.3 | |
| 0 to 0.010 |
| Lead (Pb), % | 0 to 0.020 | |
| 0 |
| Manganese (Mn), % | 1.2 to 2.0 | |
| 0 |
| Molybdenum (Mo), % | 0 | |
| 99.9 to 100 |
| Nickel (Ni), % | 4.0 to 4.8 | |
| 0 to 0.0050 |
| Nitrogen (N), % | 0 | |
| 0 to 0.0020 |
| Oxygen (O), % | 0 | |
| 0 to 0.0070 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.010 |
| Residuals, % | 0 to 0.5 | |
| 0 |