C63200 Bronze vs. C96600 Copper
Both C63200 bronze and C96600 copper are copper alloys. They have 73% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C63200 bronze and the bottom bar is C96600 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 140 |
| Elongation at Break, % | 17 to 18 | |
| 7.0 |
| Poisson's Ratio | 0.34 | |
| 0.33 |
| Shear Modulus, GPa | 44 | |
| 52 |
| Tensile Strength: Ultimate (UTS), MPa | 640 to 710 | |
| 760 |
| Tensile Strength: Yield (Proof), MPa | 310 to 350 | |
| 480 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 240 |
| Maximum Temperature: Mechanical, °C | 230 | |
| 280 |
| Melting Completion (Liquidus), °C | 1060 | |
| 1180 |
| Melting Onset (Solidus), °C | 1040 | |
| 1100 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 400 |
| Thermal Conductivity, W/m-K | 35 | |
| 30 |
| Thermal Expansion, µm/m-K | 18 | |
| 15 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 4.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.6 | |
| 4.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 65 |
| Density, g/cm3 | 8.3 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 7.0 |
| Embodied Energy, MJ/kg | 55 | |
| 100 |
| Embodied Water, L/kg | 380 | |
| 280 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 95 to 99 | |
| 47 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 400 to 510 | |
| 830 |
| Stiffness to Weight: Axial, points | 7.9 | |
| 8.7 |
| Stiffness to Weight: Bending, points | 20 | |
| 20 |
| Strength to Weight: Axial, points | 21 to 24 | |
| 24 |
| Strength to Weight: Bending, points | 20 to 21 | |
| 21 |
| Thermal Diffusivity, mm2/s | 9.6 | |
| 8.4 |
| Thermal Shock Resistance, points | 22 to 24 | |
| 25 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 8.7 to 9.5 | |
| 0 |
| Beryllium (Be), % | 0 | |
| 0.4 to 0.7 |
| Copper (Cu), % | 78.8 to 82.6 | |
| 63.5 to 69.8 |
| Iron (Fe), % | 3.5 to 4.3 | |
| 0.8 to 1.1 |
| Lead (Pb), % | 0 to 0.020 | |
| 0 to 0.010 |
| Manganese (Mn), % | 1.2 to 2.0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 4.0 to 4.8 | |
| 29 to 33 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.15 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.5 |