C63800 Bronze vs. C19000 Copper
Both C63800 bronze and C19000 copper are copper alloys. They have a moderately high 95% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C63800 bronze and the bottom bar is C19000 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 120 |
| Elongation at Break, % | 7.9 to 41 | |
| 2.5 to 50 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Rockwell B Hardness | 94 to 110 | |
| 45 to 94 |
| Shear Modulus, GPa | 43 | |
| 43 |
| Shear Strength, MPa | 320 to 500 | |
| 170 to 390 |
| Tensile Strength: Ultimate (UTS), MPa | 460 to 1010 | |
| 260 to 760 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 200 |
| Melting Completion (Liquidus), °C | 1030 | |
| 1080 |
| Melting Onset (Solidus), °C | 1000 | |
| 1040 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 390 |
| Thermal Conductivity, W/m-K | 40 | |
| 250 |
| Thermal Expansion, µm/m-K | 17 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 10 | |
| 60 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 10 | |
| 61 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 31 |
| Density, g/cm3 | 8.6 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 2.7 |
| Embodied Energy, MJ/kg | 45 | |
| 42 |
| Embodied Water, L/kg | 330 | |
| 310 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.4 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 19 | |
| 18 |
| Strength to Weight: Axial, points | 15 to 33 | |
| 8.2 to 24 |
| Strength to Weight: Bending, points | 15 to 26 | |
| 10 to 21 |
| Thermal Diffusivity, mm2/s | 11 | |
| 73 |
| Thermal Shock Resistance, points | 17 to 36 | |
| 9.3 to 27 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 2.5 to 3.1 | |
| 0 |
| Cobalt (Co), % | 0.25 to 0.55 | |
| 0 |
| Copper (Cu), % | 92.4 to 95.8 | |
| 96.9 to 99 |
| Iron (Fe), % | 0 to 0.2 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 |
| Nickel (Ni), % | 0 to 0.2 | |
| 0.9 to 1.3 |
| Phosphorus (P), % | 0 | |
| 0.15 to 0.35 |
| Silicon (Si), % | 1.5 to 2.1 | |
| 0 |
| Zinc (Zn), % | 0 to 0.8 | |
| 0 to 0.8 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.5 |