C64800 Bronze vs. ASTM Grade HG10 MNN Steel
C64800 bronze belongs to the copper alloys classification, while ASTM grade HG10 MNN steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C64800 bronze and the bottom bar is ASTM grade HG10 MNN steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 200 |
| Elongation at Break, % | 8.0 | |
| 23 |
| Poisson's Ratio | 0.34 | |
| 0.28 |
| Shear Modulus, GPa | 44 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 640 | |
| 590 |
| Tensile Strength: Yield (Proof), MPa | 630 | |
| 250 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 990 |
| Melting Completion (Liquidus), °C | 1090 | |
| 1420 |
| Melting Onset (Solidus), °C | 1030 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 480 |
| Thermal Conductivity, W/m-K | 260 | |
| 15 |
| Thermal Expansion, µm/m-K | 17 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 65 | |
| 2.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 66 | |
| 2.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 21 |
| Density, g/cm3 | 8.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 4.0 |
| Embodied Energy, MJ/kg | 43 | |
| 58 |
| Embodied Water, L/kg | 310 | |
| 160 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 51 | |
| 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1680 | |
| 160 |
| Stiffness to Weight: Axial, points | 7.4 | |
| 14 |
| Stiffness to Weight: Bending, points | 18 | |
| 25 |
| Strength to Weight: Axial, points | 20 | |
| 21 |
| Strength to Weight: Bending, points | 19 | |
| 20 |
| Thermal Diffusivity, mm2/s | 75 | |
| 3.9 |
| Thermal Shock Resistance, points | 23 | |
| 13 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 | |
| 0.070 to 0.11 |
| Chromium (Cr), % | 0 to 0.090 | |
| 18.5 to 20.5 |
| Cobalt (Co), % | 1.0 to 3.0 | |
| 0 |
| Copper (Cu), % | 92.4 to 98.8 | |
| 0 to 0.5 |
| Iron (Fe), % | 0 to 1.0 | |
| 57.9 to 66.5 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 3.0 to 5.0 |
| Molybdenum (Mo), % | 0 | |
| 0.25 to 0.45 |
| Nickel (Ni), % | 0 to 0.5 | |
| 11.5 to 13.5 |
| Niobium (Nb), % | 0 | |
| 0.2 to 1.0 |
| Nitrogen (N), % | 0 | |
| 0.2 to 0.3 |
| Phosphorus (P), % | 0 to 0.5 | |
| 0 to 0.040 |
| Silicon (Si), % | 0.2 to 1.0 | |
| 0 to 0.7 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tin (Sn), % | 0 to 0.5 | |
| 0 |
| Zinc (Zn), % | 0 to 0.5 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |