C65100 Bronze vs. C26000 Brass
Both C65100 bronze and C26000 brass are copper alloys. They have 71% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C65100 bronze and the bottom bar is C26000 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Elongation at Break, % | 2.4 to 50 | |
| 2.5 to 66 |
| Poisson's Ratio | 0.34 | |
| 0.31 |
| Shear Modulus, GPa | 43 | |
| 41 |
| Shear Strength, MPa | 200 to 350 | |
| 230 to 390 |
| Tensile Strength: Ultimate (UTS), MPa | 280 to 560 | |
| 320 to 680 |
| Tensile Strength: Yield (Proof), MPa | 95 to 440 | |
| 110 to 570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 180 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 140 |
| Melting Completion (Liquidus), °C | 1060 | |
| 950 |
| Melting Onset (Solidus), °C | 1030 | |
| 920 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 57 | |
| 120 |
| Thermal Expansion, µm/m-K | 18 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 12 | |
| 28 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 12 | |
| 31 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 25 |
| Density, g/cm3 | 8.8 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 2.7 |
| Embodied Energy, MJ/kg | 41 | |
| 45 |
| Embodied Water, L/kg | 300 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 110 | |
| 6.1 to 420 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 39 to 820 | |
| 51 to 1490 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 18 | |
| 19 |
| Strength to Weight: Axial, points | 8.7 to 18 | |
| 11 to 23 |
| Strength to Weight: Bending, points | 11 to 17 | |
| 13 to 21 |
| Thermal Diffusivity, mm2/s | 16 | |
| 38 |
| Thermal Shock Resistance, points | 9.5 to 19 | |
| 11 to 23 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Bismuth (Bi), % | 0 | |
| 0 to 0.0059 |
| Copper (Cu), % | 94.5 to 99.2 | |
| 68.5 to 71.5 |
| Iron (Fe), % | 0 to 0.8 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.070 |
| Manganese (Mn), % | 0 to 0.7 | |
| 0 |
| Silicon (Si), % | 0.8 to 2.0 | |
| 0 |
| Zinc (Zn), % | 0 to 1.5 | |
| 28.1 to 31.5 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.3 |