C65500 Bronze vs. ASTM A204 Steel
C65500 bronze belongs to the copper alloys classification, while ASTM A204 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C65500 bronze and the bottom bar is ASTM A204 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 190 |
| Elongation at Break, % | 4.0 to 70 | |
| 18 to 22 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 43 | |
| 73 |
| Shear Strength, MPa | 260 to 440 | |
| 330 to 360 |
| Tensile Strength: Ultimate (UTS), MPa | 360 to 760 | |
| 520 to 590 |
| Tensile Strength: Yield (Proof), MPa | 120 to 430 | |
| 290 to 330 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 410 |
| Melting Completion (Liquidus), °C | 1030 | |
| 1470 |
| Melting Onset (Solidus), °C | 970 | |
| 1420 to 1430 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 470 |
| Thermal Conductivity, W/m-K | 36 | |
| 52 |
| Thermal Expansion, µm/m-K | 18 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.3 | |
| 8.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 2.4 |
| Density, g/cm3 | 8.6 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 1.5 |
| Embodied Energy, MJ/kg | 42 | |
| 20 |
| Embodied Water, L/kg | 300 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 11 to 450 | |
| 90 to 95 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 62 to 790 | |
| 220 to 290 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 |
| Strength to Weight: Axial, points | 12 to 24 | |
| 18 to 21 |
| Strength to Weight: Bending, points | 13 to 21 | |
| 18 to 20 |
| Thermal Diffusivity, mm2/s | 10 | |
| 14 |
| Thermal Shock Resistance, points | 12 to 26 | |
| 15 to 17 |