C66100 Bronze vs. C95410 Bronze
Both C66100 bronze and C95410 bronze are copper alloys. They have 85% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C66100 bronze and the bottom bar is C95410 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Elongation at Break, % | 8.0 to 40 | |
| 9.1 to 13 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 43 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 410 to 790 | |
| 620 to 740 |
| Tensile Strength: Yield (Proof), MPa | 120 to 430 | |
| 260 to 380 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 230 |
| Melting Completion (Liquidus), °C | 1050 | |
| 1040 |
| Melting Onset (Solidus), °C | 1000 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 440 |
| Thermal Conductivity, W/m-K | 34 | |
| 59 |
| Thermal Expansion, µm/m-K | 17 | |
| 18 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 28 |
| Density, g/cm3 | 8.7 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 3.3 |
| Embodied Energy, MJ/kg | 42 | |
| 54 |
| Embodied Water, L/kg | 300 | |
| 390 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 53 to 120 | |
| 57 to 64 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 60 to 790 | |
| 280 to 630 |
| Stiffness to Weight: Axial, points | 7.4 | |
| 7.8 |
| Stiffness to Weight: Bending, points | 19 | |
| 20 |
| Strength to Weight: Axial, points | 13 to 25 | |
| 21 to 25 |
| Strength to Weight: Bending, points | 14 to 22 | |
| 20 to 22 |
| Thermal Diffusivity, mm2/s | 9.7 | |
| 16 |
| Thermal Shock Resistance, points | 15 to 29 | |
| 22 to 26 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 10 to 11.5 |
| Copper (Cu), % | 92 to 97 | |
| 83 to 85.5 |
| Iron (Fe), % | 0 to 0.25 | |
| 3.0 to 5.0 |
| Lead (Pb), % | 0.2 to 0.8 | |
| 0 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 | |
| 1.5 to 2.5 |
| Silicon (Si), % | 2.8 to 3.5 | |
| 0 |
| Zinc (Zn), % | 0 to 1.5 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.5 |