C66200 Brass vs. C49300 Brass
Both C66200 brass and C49300 brass are copper alloys. They have 71% of their average alloy composition in common.
For each property being compared, the top bar is C66200 brass and the bottom bar is C49300 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 100 |
| Elongation at Break, % | 8.0 to 15 | |
| 4.5 to 20 |
| Poisson's Ratio | 0.33 | |
| 0.31 |
| Shear Modulus, GPa | 42 | |
| 40 |
| Shear Strength, MPa | 270 to 300 | |
| 270 to 290 |
| Tensile Strength: Ultimate (UTS), MPa | 450 to 520 | |
| 430 to 520 |
| Tensile Strength: Yield (Proof), MPa | 410 to 480 | |
| 210 to 410 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 120 |
| Melting Completion (Liquidus), °C | 1070 | |
| 880 |
| Melting Onset (Solidus), °C | 1030 | |
| 840 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 380 |
| Thermal Conductivity, W/m-K | 150 | |
| 88 |
| Thermal Expansion, µm/m-K | 18 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 35 | |
| 15 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 36 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 26 |
| Density, g/cm3 | 8.7 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 3.0 |
| Embodied Energy, MJ/kg | 43 | |
| 50 |
| Embodied Water, L/kg | 320 | |
| 370 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 40 to 66 | |
| 21 to 71 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 760 to 1030 | |
| 220 to 800 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 14 to 17 | |
| 15 to 18 |
| Strength to Weight: Bending, points | 15 to 16 | |
| 16 to 18 |
| Thermal Diffusivity, mm2/s | 45 | |
| 29 |
| Thermal Shock Resistance, points | 16 to 18 | |
| 14 to 18 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 0.5 |
| Antimony (Sb), % | 0 | |
| 0 to 0.5 |
| Bismuth (Bi), % | 0 | |
| 0.5 to 2.0 |
| Copper (Cu), % | 86.6 to 91 | |
| 58 to 62 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.010 |
| Manganese (Mn), % | 0 | |
| 0 to 0.030 |
| Nickel (Ni), % | 0.3 to 1.0 | |
| 0 to 1.5 |
| Phosphorus (P), % | 0.050 to 0.2 | |
| 0 to 0.2 |
| Selenium (Se), % | 0 | |
| 0 to 0.2 |
| Silicon (Si), % | 0 | |
| 0 to 0.1 |
| Tin (Sn), % | 0.2 to 0.7 | |
| 1.0 to 1.8 |
| Zinc (Zn), % | 6.5 to 12.9 | |
| 30.6 to 40.5 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.5 |