C67000 Bronze vs. C51100 Bronze
Both C67000 bronze and C51100 bronze are copper alloys. They have 66% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C67000 bronze and the bottom bar is C51100 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 5.6 to 11 | |
| 2.5 to 50 |
| Poisson's Ratio | 0.31 | |
| 0.34 |
| Shear Modulus, GPa | 42 | |
| 42 |
| Shear Strength, MPa | 390 to 510 | |
| 230 to 410 |
| Tensile Strength: Ultimate (UTS), MPa | 660 to 880 | |
| 330 to 720 |
| Tensile Strength: Yield (Proof), MPa | 350 to 540 | |
| 93 to 700 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 190 |
| Melting Completion (Liquidus), °C | 900 | |
| 1060 |
| Melting Onset (Solidus), °C | 850 | |
| 970 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 380 |
| Thermal Conductivity, W/m-K | 99 | |
| 84 |
| Thermal Expansion, µm/m-K | 20 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 22 | |
| 20 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 25 | |
| 20 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 32 |
| Density, g/cm3 | 7.9 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 3.0 |
| Embodied Energy, MJ/kg | 49 | |
| 48 |
| Embodied Water, L/kg | 350 | |
| 340 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 43 to 62 | |
| 18 to 140 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 560 to 1290 | |
| 38 to 2170 |
| Stiffness to Weight: Axial, points | 7.8 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 20 | |
| 18 |
| Strength to Weight: Axial, points | 23 to 31 | |
| 10 to 22 |
| Strength to Weight: Bending, points | 21 to 26 | |
| 12 to 20 |
| Thermal Diffusivity, mm2/s | 30 | |
| 25 |
| Thermal Shock Resistance, points | 21 to 29 | |
| 12 to 26 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 3.0 to 6.0 | |
| 0 |
| Copper (Cu), % | 63 to 68 | |
| 93.8 to 96.5 |
| Iron (Fe), % | 2.0 to 4.0 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 to 0.2 | |
| 0 to 0.050 |
| Manganese (Mn), % | 2.5 to 5.0 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0.030 to 0.35 |
| Tin (Sn), % | 0 to 0.5 | |
| 3.5 to 4.9 |
| Zinc (Zn), % | 21.8 to 32.5 | |
| 0 to 0.3 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.5 |