C67300 Bronze vs. Nickel 690
C67300 bronze belongs to the copper alloys classification, while nickel 690 belongs to the nickel alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C67300 bronze and the bottom bar is nickel 690.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 200 |
| Elongation at Break, % | 12 | |
| 3.4 to 34 |
| Poisson's Ratio | 0.31 | |
| 0.28 |
| Shear Modulus, GPa | 41 | |
| 79 |
| Shear Strength, MPa | 300 | |
| 420 to 570 |
| Tensile Strength: Ultimate (UTS), MPa | 500 | |
| 640 to 990 |
| Tensile Strength: Yield (Proof), MPa | 340 | |
| 250 to 760 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 130 | |
| 1010 |
| Melting Completion (Liquidus), °C | 870 | |
| 1380 |
| Melting Onset (Solidus), °C | 830 | |
| 1340 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 470 |
| Thermal Conductivity, W/m-K | 95 | |
| 14 |
| Thermal Expansion, µm/m-K | 20 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 22 | |
| 1.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 25 | |
| 1.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 50 |
| Density, g/cm3 | 8.0 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 8.2 |
| Embodied Energy, MJ/kg | 46 | |
| 120 |
| Embodied Water, L/kg | 320 | |
| 290 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 55 | |
| 31 to 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 550 | |
| 160 to 1440 |
| Stiffness to Weight: Axial, points | 7.4 | |
| 13 |
| Stiffness to Weight: Bending, points | 20 | |
| 24 |
| Strength to Weight: Axial, points | 17 | |
| 21 to 33 |
| Strength to Weight: Bending, points | 17 | |
| 20 to 27 |
| Thermal Diffusivity, mm2/s | 30 | |
| 3.5 |
| Thermal Shock Resistance, points | 16 | |
| 16 to 25 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.25 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 | |
| 27 to 31 |
| Copper (Cu), % | 58 to 63 | |
| 0 to 0.5 |
| Iron (Fe), % | 0 to 0.5 | |
| 7.0 to 11 |
| Lead (Pb), % | 0.4 to 3.0 | |
| 0 |
| Manganese (Mn), % | 2.0 to 3.5 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 to 0.25 | |
| 58 to 66 |
| Silicon (Si), % | 0.5 to 1.5 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Tin (Sn), % | 0 to 0.3 | |
| 0 |
| Zinc (Zn), % | 27.2 to 39.1 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |