C67500 Bronze vs. Grade 18 Titanium
C67500 bronze belongs to the copper alloys classification, while grade 18 titanium belongs to the titanium alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C67500 bronze and the bottom bar is grade 18 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 110 |
| Elongation at Break, % | 14 to 33 | |
| 11 to 17 |
| Poisson's Ratio | 0.3 | |
| 0.32 |
| Shear Modulus, GPa | 40 | |
| 40 |
| Shear Strength, MPa | 270 to 350 | |
| 420 to 590 |
| Tensile Strength: Ultimate (UTS), MPa | 430 to 580 | |
| 690 to 980 |
| Tensile Strength: Yield (Proof), MPa | 170 to 370 | |
| 540 to 810 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 330 |
| Melting Completion (Liquidus), °C | 890 | |
| 1640 |
| Melting Onset (Solidus), °C | 870 | |
| 1590 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 550 |
| Thermal Conductivity, W/m-K | 110 | |
| 8.3 |
| Thermal Expansion, µm/m-K | 21 | |
| 9.9 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 24 | |
| 1.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 27 | |
| 2.7 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.0 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 41 |
| Embodied Energy, MJ/kg | 47 | |
| 670 |
| Embodied Water, L/kg | 330 | |
| 270 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 61 to 130 | |
| 87 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 to 650 | |
| 1380 to 3110 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 13 |
| Stiffness to Weight: Bending, points | 20 | |
| 35 |
| Strength to Weight: Axial, points | 15 to 20 | |
| 43 to 61 |
| Strength to Weight: Bending, points | 16 to 19 | |
| 39 to 49 |
| Thermal Diffusivity, mm2/s | 34 | |
| 3.4 |
| Thermal Shock Resistance, points | 14 to 19 | |
| 47 to 67 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.25 | |
| 2.5 to 3.5 |
| Carbon (C), % | 0 | |
| 0 to 0.080 |
| Copper (Cu), % | 57 to 60 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 0.8 to 2.0 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 to 0.2 | |
| 0 |
| Manganese (Mn), % | 0.050 to 0.5 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.15 |
| Palladium (Pd), % | 0 | |
| 0.040 to 0.080 |
| Tin (Sn), % | 0.5 to 1.5 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 92.5 to 95.5 |
| Vanadium (V), % | 0 | |
| 2.0 to 3.0 |
| Zinc (Zn), % | 35.1 to 41.7 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.4 |