C67500 Bronze vs. SAE-AISI 1084 Steel
C67500 bronze belongs to the copper alloys classification, while SAE-AISI 1084 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C67500 bronze and the bottom bar is SAE-AISI 1084 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 190 |
| Elongation at Break, % | 14 to 33 | |
| 11 |
| Poisson's Ratio | 0.3 | |
| 0.29 |
| Shear Modulus, GPa | 40 | |
| 72 |
| Shear Strength, MPa | 270 to 350 | |
| 470 to 550 |
| Tensile Strength: Ultimate (UTS), MPa | 430 to 580 | |
| 780 to 930 |
| Tensile Strength: Yield (Proof), MPa | 170 to 370 | |
| 510 to 600 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 240 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 400 |
| Melting Completion (Liquidus), °C | 890 | |
| 1450 |
| Melting Onset (Solidus), °C | 870 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 470 |
| Thermal Conductivity, W/m-K | 110 | |
| 51 |
| Thermal Expansion, µm/m-K | 21 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 24 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 27 | |
| 8.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 1.8 |
| Density, g/cm3 | 8.0 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 1.4 |
| Embodied Energy, MJ/kg | 47 | |
| 19 |
| Embodied Water, L/kg | 330 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 61 to 130 | |
| 81 to 89 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 to 650 | |
| 700 to 960 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 13 |
| Stiffness to Weight: Bending, points | 20 | |
| 24 |
| Strength to Weight: Axial, points | 15 to 20 | |
| 28 to 33 |
| Strength to Weight: Bending, points | 16 to 19 | |
| 24 to 27 |
| Thermal Diffusivity, mm2/s | 34 | |
| 14 |
| Thermal Shock Resistance, points | 14 to 19 | |
| 25 to 30 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.25 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.8 to 0.93 |
| Copper (Cu), % | 57 to 60 | |
| 0 |
| Iron (Fe), % | 0.8 to 2.0 | |
| 98.1 to 98.6 |
| Lead (Pb), % | 0 to 0.2 | |
| 0 |
| Manganese (Mn), % | 0.050 to 0.5 | |
| 0.6 to 0.9 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Sulfur (S), % | 0 | |
| 0 to 0.050 |
| Tin (Sn), % | 0.5 to 1.5 | |
| 0 |
| Zinc (Zn), % | 35.1 to 41.7 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |