C67500 Bronze vs. C67600 Bronze
Both C67500 bronze and C67600 bronze are copper alloys. Their average alloy composition is basically identical.
For each property being compared, the top bar is C67500 bronze and the bottom bar is C67600 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 100 |
| Elongation at Break, % | 14 to 33 | |
| 13 to 33 |
| Poisson's Ratio | 0.3 | |
| 0.31 |
| Shear Modulus, GPa | 40 | |
| 40 |
| Shear Strength, MPa | 270 to 350 | |
| 270 to 350 |
| Tensile Strength: Ultimate (UTS), MPa | 430 to 580 | |
| 430 to 570 |
| Tensile Strength: Yield (Proof), MPa | 170 to 370 | |
| 170 to 380 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 120 |
| Melting Completion (Liquidus), °C | 890 | |
| 890 |
| Melting Onset (Solidus), °C | 870 | |
| 870 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 380 |
| Thermal Conductivity, W/m-K | 110 | |
| 110 |
| Thermal Expansion, µm/m-K | 21 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 24 | |
| 24 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 27 | |
| 27 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 23 |
| Density, g/cm3 | 8.0 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 2.8 |
| Embodied Energy, MJ/kg | 47 | |
| 47 |
| Embodied Water, L/kg | 330 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 61 to 130 | |
| 63 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 to 650 | |
| 140 to 680 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 20 | |
| 20 |
| Strength to Weight: Axial, points | 15 to 20 | |
| 15 to 20 |
| Strength to Weight: Bending, points | 16 to 19 | |
| 16 to 19 |
| Thermal Diffusivity, mm2/s | 34 | |
| 35 |
| Thermal Shock Resistance, points | 14 to 19 | |
| 14 to 19 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.25 | |
| 0 |
| Copper (Cu), % | 57 to 60 | |
| 57 to 60 |
| Iron (Fe), % | 0.8 to 2.0 | |
| 0.4 to 1.3 |
| Lead (Pb), % | 0 to 0.2 | |
| 0.5 to 1.0 |
| Manganese (Mn), % | 0.050 to 0.5 | |
| 0.050 to 0.5 |
| Tin (Sn), % | 0.5 to 1.5 | |
| 0.5 to 1.5 |
| Zinc (Zn), % | 35.1 to 41.7 | |
| 35.2 to 41.6 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.5 |